LTL Color Compounds ColorFast® FRA203 ABS
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | LTL Color Compounds |
| Trade Name | ColorFast® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LTL Color Compounds ColorFast® FRA203 ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Business machinery V0 ABS with excellent indoor light stabilityAll information provided by LTL Color Compounders, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in | 0.125; ASTM D955 |
| Melt Flow | 5.0 g/10 min @Load 3.80 kg, Temperature 230 °C |
5.0 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 95 | 95 | ASTM D785 |
| Tensile Strength, Yield | 41.4 MPa | 6000 psi | 2.0 in/min; ASTM D638 |
| Elongation at Break | 15 % | 15 % | 2.0 in/min; ASTM D638 |
| Flexural Strength | 63.4 MPa | 9200 psi | 2.0 in/min; ASTM D790 |
| Flexural Modulus | 2.28 GPa | 330 ksi | 2.0 in/min; ASTM D790 |
| Izod Impact, Notched | 2.67 J/cm @Temperature 22.8 °C |
5.00 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 76.7 °C | 170 °F | Unannealed (0.250"); ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 2.30 mm |
V-0 @Thickness 0.0906 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 171 - 182 °C | 340 - 360 °F | |
| Middle Barrel Temperature | 199 - 210 °C | 390 - 410 °F | |
| Front Barrel Temperature | 210 - 221 °C | 410 - 430 °F | |
| Nozzle Temperature | 193 - 221 °C | 380 - 430 °F | |
| Melt Temperature | 193 - 232 °C | 380 - 450 °F | |
| Mold Temperature | 71.1 - 82.2 °C | 160 - 180 °F | |
| Drying Temperature | 71.1 - 82.2 °C | 160 - 180 °F | |
| Dry Time | 3 - 4 hour | 3 - 4 hour | nominal; maximum drying time of 8 hours |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi | |
| Shot Size | 50 - 70 % | 50 - 70 % | |
| Vent Depth | 0.00381 - 0.00508 cm | 0.00150 - 0.00200 in | |
| Screw Speed | 30 - 60 rpm | 30 - 60 rpm |
Users viewing this material also viewed the following:
- Premix Premi-Glas® 2200-20 CR-SX Fiberglass Reinforced Thermoset SMC
- Mitsui AURUM® JCL3030 Thermoplastic Polyimide Resin, Amorphous, Wear/Friction Grade (discontinued **)
- LG Chemical SEETEC H7511 Polypropylene, Homopolymer
- Microtherm Group Marineguard® Filament Reinforced Silica Marine Insulation Panel, Flexible and Waterproof
- STAR Thermoplastic Alloys & Rubbers StarMediflex P 7050-1000 TPE
- Techmer ES Electrablend® PA12 Stainless Steel Filled
- Teknor Apex Sinpolene MBW108LE Low Density Polyethylene
- A. Schulman ComAlloy® E-12421 Reinforced High Flow Polyamide
- Aremco Ceramacast™ 575 Alumina Fine Grain Potting Compound
- Touchstone MetPreg™ Fiber Reinforced Aluminum