LNP Konduit® ITF-212-11 Polyamide 6/12 Copolymer  (discontinued **)

Category Polymer , Thermoplastic , Nylon , Nylon 612 , Nylon 612, Unreinforced
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LNP Konduit® ITF-212-11 Polyamide 6/12 Copolymer  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features: Thermally ConductiveForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.
Physical Properties Metric English Comments
Linear Mold Shrinkage 0.0090 cm/cm
0.0090 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.015 cm/cm
0.015 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 79.3 MPa
11500 psi
ASTM D638
Tensile Strength, Yield 79.3 MPa
11500 psi
ASTM D638
Elongation at Break 2.1 %
2.1 %
ASTM D638
Elongation at Yield 2.1 %
2.1 %
ASTM D638
Tensile Modulus 9.98 GPa
1450 ksi
ASTM D638
Flexural Strength 145 MPa
21000 psi
ASTM D790
Flexural Modulus 9.26 GPa
1340 ksi
ASTM D790
Izod Impact, Notched 0.320 J/cm

@Thickness 3.18 mm
0.599 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Unnotched 4.22 J/cm

@Thickness 3.18 mm
7.91 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Notched (ISO) 4.20 kJ/m²
2.00 ft-lb/in²
ISO 180
Izod Impact, Unnotched (ISO) 28.1 kJ/m²
13.4 ft-lb/in²
ISO 180
Falling Dart Impact 8.47 J
6.25 ft-lb
ASTM D3763
Impact Test 1.92 J
1.42 ft-lb
Multi-Axial Instrumented Impact Energy; ISO 6603-2
Thermal Properties Metric English Comments
Thermal Conductivity 1.10 W/m-K
7.63 BTU-in/hr-ft²-°F
Tested in accordance with ASTM F433; ASTM C177
Deflection Temperature at 1.8 MPa (264 psi) 168 °C
334 °F
Unannealed; ASTM D648
Processing Properties Metric English Comments
Melt Temperature 268 - 274 °C
514 - 525 °F
Mold Temperature 65.6 - 93.3 °C
150 - 200 °F
Drying Temperature 82.2 °C
180 °F
Dry Time 4 hour
4 hour
Moisture Content 0.020 %
0.020 %
Suggested
Back Pressure 0.172 - 0.345 MPa
24.9 - 50.0 psi