SABIC Innovative Plastics LNP Lubricomp WL0049XF PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), PTFE Filled |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Lubricomp WL0049XF PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Lubricomp* WL0049 is a compound based on Polybutylene Terephalate resin containing PTFE and Flame Retardant. Added features include: Internally Lubricated, Flame Retardant.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.52 g/cc | 0.0549 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.021 cm/cm | 0.021 in/in | SABIC Method |
| 0.00070 cm/cm @Time 86400 sec |
0.00070 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 43.0 MPa | 6240 psi | 5 mm/min; ISO 527 |
| Tensile Strength, Yield | 43.0 MPa | 6240 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 6.3 % | 6.3 % | Flexural Strain, 2 mm/min; ISO 178 |
| Elongation at Yield | 3.8 % | 3.8 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 2.50 GPa | 363 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 73.0 MPa | 10600 psi | 2 mm/min; ISO 178 |
| Flexural Yield Strength | 73.0 MPa | 10600 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.30 GPa | 334 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² @Temperature 23.0 °C |
1.43 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 30.0 kJ/m² @Temperature 23.0 °C |
14.3 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 109 µm/m-°C @Temperature 23.0 - 60.0 °C |
60.6 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 101 µm/m-°C @Temperature 23.0 - 60.0 °C |
56.1 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 63.0 °C | 145 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
UL 94 by SABIC-IP |
Users viewing this material also viewed the following:
- Outokumpu 4432 Cr-Ni-Mo Austenitic Stainless Steel
- Park Electrochemical Nelcote® E-765 Epoxy Prepreg, 7781 E-Glass Reinforced
- Polymer Industries Densetec PP Copolymer Sheet
- DSM Akulon® Ultraflow™ K-FG12 Nylon 6-60% Glass Reinforced (European Grade) (Dry) (discontinued **)
- Huntsman Araldite GZ 571 KX-75 Bisphenol A Epoxy Solution
- Borealis BL0521 High Density Polyethylene
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 0.5 PHR Sulfur
- Cheng Yu Plastic PP237G2 Polypropylene, 20% Glass Fiber
- CP-Polymer-Technik Wellamid® 6600/42 HWCP Nylon 66, Polymer Modified, Heat Stabilized, Conditioned
- Kleerdex Kydex® 160 Acrylic/PVC Thermoplastic Sheet (discontinued **)
Copyright © lookpolymers.com All Rights Reserved