LG Chemical Lupox® SG5200 PBT+PET+GF20%
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , PBT + PET Blend, Glass Filled , Polyethylene Terephthalate (PET) |
| Manufacturer | LG Chemical |
| Trade Name | Lupox® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical Lupox® SG5200 PBT+PET+GF20%.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding, PBT+PET+GF20%, Good Surface Application: E&E (Microwave Oven Door Gasket)CAS No. 65997-17-3, 25038-59-9 and 24968-12-5Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.45 g/cc | 1.45 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.020 | 0.020 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.010 cm/cm @Thickness 3.20 mm |
0.0040 - 0.010 in/in @Thickness 0.126 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 98.1 MPa @Thickness 3.20 mm |
14200 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | 3.0 % @Thickness 3.20 mm |
3.0 % @Thickness 0.126 in |
5mm/min; ASTM D638 |
| Flexural Yield Strength | 152 MPa @Thickness 3.20 mm |
22000 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| Flexural Modulus | 5.69 GPa @Thickness 3.20 mm |
825 ksi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| Izod Impact, Notched | 0.539 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
1.01 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 225 °C | 437 °F | @ Break; ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C @Thickness 6.40 mm |
410 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C @Thickness 6.40 mm |
392 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| UL RTI, Electrical | 75.0 °C @Thickness >=1.50 mm |
167 °F @Thickness >=0.0591 in |
|
| UL RTI, Mechanical with Impact | 75.0 °C @Thickness >=1.50 mm |
167 °F @Thickness >=0.0591 in |
|
| UL RTI, Mechanical without Impact | 75.0 °C @Thickness >=1.50 mm |
167 °F @Thickness >=0.0591 in |
|
| Flammability, UL94 | HB @Thickness >=1.50 mm |
HB @Thickness >=0.0591 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 245 - 255 °C | 473 - 491 °F | Injection Molding |
| Middle Barrel Temperature | 250 - 260 °C | 482 - 500 °F | Injection Molding |
| Front Barrel Temperature | 255 - 265 °C | 491 - 509 °F | Injection Molding |
| Nozzle Temperature | 255 - 265 °C | 491 - 509 °F | Injection Molding |
| Melt Temperature | 255 - 265 °C | 491 - 509 °F | Injection Molding |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | Injection Molding |
| Drying Temperature | 120 °C | 248 °F | Injection Molding |
| Dry Time | 4.00 - 5.00 hour | 4.00 - 5.00 hour | Injection Molding |
Users viewing this material also viewed the following:
- PolyOne Novablend™ 9562 Polyvinyl Chloride Alloy (PVC Alloy)
- Polymer Resources TPSF-FRG10 Polybutylene Terephthalate, Structural Foam, 10% Glass Reinforced, Flame Retardant
- Lord Adhesives CircuitSAFâ„¢ MA-420 Epoxy Surface Mount Adhesive
- Schwartz Technical Plastics LAMIGAMID® 410 Cast Polyamide 6, Elastomer Modified, Low Temp, Dry
- SABIC Innovative Plastics LNP Stat-kon ZE004 MODIFIED POYPHENYLENE
- Teknor Apex Monprene® MP-1870A Thermoplastic Elastomer
- A. Schulman ComAlloy® E-14961 30% Glass Fiber Reinforced Polycarbonate
- ExxonMobil PP7505KNE2 Polypropylene Homopolymer
- ALM PA 250 Nylon 12 SLS Prototyping Polymer
- A. Schulman ComAlloy Hiloy® 212 Polystyrene, Glass Reinforced
Copyright © lookpolymers.com All Rights Reserved