LG Chemical Lupox® PBT-HI1002FM Impact Modified, Flame Retardant PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Flame Retardant |
| Manufacturer | LG Chemical |
| Trade Name | Lupox® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical Lupox® PBT-HI1002FM Impact Modified, Flame Retardant PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by US distributor Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 50.3 MPa | 7300 psi | ASTM D638 |
| Elongation at Break | 30 % | 30 % | ASTM D638 |
| Flexural Yield Strength | 78.1 MPa @Thickness 3.17 mm |
11300 psi @Thickness 0.125 in |
ASTM D790 |
| Flexural Modulus | 1.93 GPa @Thickness 3.17 mm |
280 ksi @Thickness 0.125 in |
ASTM D790 |
| Izod Impact, Notched | 1.66 J/cm @Thickness 3.17 mm |
3.11 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C | 207 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 0.7937 mm |
V-0 @Thickness 0.03125 in |
UL94 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 240 - 260 °C | 464 - 500 °F | |
| Middle Barrel Temperature | 250 - 270 °C | 482 - 518 °F | |
| Front Barrel Temperature | 250 - 270 °C | 482 - 518 °F | |
| Nozzle Temperature | 260 - 280 °C | 500 - 536 °F | |
| Melt Temperature | 260 - 280 °C | 500 - 536 °F | |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | Surface |
| Drying Temperature | 120 °C | 248 °F | 5 hr. |
| 140 °C | 284 °F | 3 hr. | |
| 120 °C @Time 18000 sec |
248 °F @Time 5.00 hour |
||
| 140 °C @Time 10800 sec |
284 °F @Time 3.00 hour |
||
| Injection Pressure | 41.4 - 62.1 MPa | 6000 - 9000 psi | Second |
| 48.3 - 75.8 MPa | 7000 - 11000 psi | First | |
| Back Pressure | 0.000 - 0.345 MPa | 0.000 - 50.0 psi | |
| Shot Size | 40 - 80 % | 40 - 80 % | |
| Vent Depth | 0.00254 - 0.00381 cm | 0.00100 - 0.00150 in |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ram Speed Setting | Medium to Fast | |
| Screw Speed | Medium |
Users viewing this material also viewed the following:
- Rochling Engineered Plastics Polystone® G HDPE Extruded Sheet
- Network Polymers MS 160 Styrene Methyl Methacrylate Terpolymer
- Petroquimica Triunfo Trithene® TS 9022 MDPE - Overwrap Packaging
- LyondellBasell Microthene® F FN51000 Low Density Polyethylene
- Lotte Chemical Titan TITANPRO® PD855 Polypropylene homopolymer
- Techmer ES HiFill® PA6 GF30 HS BK 30% Glass Filled
- Wellman Wellamid® WE1410 43% Glass Fiber Reinforced Nylon 66
- Loctite® 262 Medium to High Strength Threadlocker
- DuPont Performance Polymers Delrin® SC690 NC010 Acetal (POM) (Unverified Data**)
- DuPont Teijin Films Melinex® XST6562 Polyester Film, 200 Gauge
Copyright © lookpolymers.com All Rights Reserved