Global GPC-130 30% Glass Filled Polycarbonate
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 30% Glass Filled |
| Manufacturer | Global Polymers Corporation |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Global GPC-130 30% Glass Filled Polycarbonate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Global Polymers Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.44 g/cc | 0.0520 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | ASTM D955 |
| Melt Flow | 8.0 g/10 min | 8.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 124 MPa | 18000 psi | ASTM D638 |
| Flexural Modulus | 6.89 GPa | 1000 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm | 2.00 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 146 °C | 295 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Multibase Multi-Pro® 2005 XRC Black 20% Filler Content Polypropylene
- MV Labs NH200 NH4Br Ammonium bromide
- DuPont Performance Polymers Hypalon® 48 Chlorosulfonated Polyethylene Rubber, Uncured Carbon Black Filled Compound &
- Hong Kun Group 4-tert-Butyl-2,6-diisopropylphenol Pharmaceutical Intermediate
- H.C. Starck Amperit® 599.074 Agglomerated Sintered Molybdenum Carbide (Cr2O3)
- Hexcel® HexWeb® CR III 3/8-5056-.0015 Corrosion Resistant Specification Grade Aluminum Honeycomb
- Dow Corning AMS-C30 Cosmetic Wax
- Eastman Eastman 1223 Copolyester
- Braskem H 103 Injection Molding Polypropylene
- 3M 401M Double Coated Paper Tapes
Copyright © lookpolymers.com All Rights Reserved