LG Chemical Lupox® LW5402A PBT+PC+GF40%
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Glass Filled , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | LG Chemical |
| Trade Name | Lupox® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical Lupox® LW5402A PBT+PC+GF40%.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding, PBT+PC+GF40%, Low Warpage, High GlossApplication: E&E, Automotive (Bobbin, Switch)CAS No. 9010-86-0, 65997-17-3, 24968-12-5 and 103598-77-2Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.60 g/cc | 1.60 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.020 | 0.020 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0060 in/in @Thickness 0.126 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 96.1 MPa @Thickness 3.20 mm |
13900 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | 6.0 % @Thickness 3.20 mm |
6.0 % @Thickness 0.126 in |
5mm/min; ASTM D638 |
| Flexural Yield Strength | 152 MPa @Thickness 3.20 mm |
22000 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| Flexural Modulus | 7.85 GPa @Thickness 3.20 mm |
1140 ksi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| Izod Impact, Notched | 0.735 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
1.38 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 225 °C | 437 °F | @ Break; ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C @Thickness 6.40 mm |
410 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C @Thickness 6.40 mm |
383 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 235 - 250 °C | 455 - 482 °F | Injection Molding |
| Middle Barrel Temperature | 240 - 250 °C | 464 - 482 °F | Injection Molding |
| Front Barrel Temperature | 245 - 255 °C | 473 - 491 °F | Injection Molding |
| Nozzle Temperature | 245 - 255 °C | 473 - 491 °F | Injection Molding |
| Melt Temperature | 245 - 255 °C | 473 - 491 °F | Injection Molding |
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | Injection Molding |
| Drying Temperature | 120 °C | 248 °F | Injection Molding |
| Dry Time | 4.00 - 5.00 hour | 4.00 - 5.00 hour | Injection Molding |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 66 GF 35 Polyamide 66, 35% Glass Fiber
- Ovation Polymers Nima™ NH PA66UT Nylon 66
- Teknor Apex APEX® 94-A0098A-75 Polyvinyl Chloride, Flexible
- Chase Plastics CP Pryme® N130GL (COND, 50% RH) Nylon 6, 30% Glass Fiber Reinforced, Internally Lubricated
- ExxonMobil LL 3003.39 Cast Film Resin
- Chosun Refractories CRS-A60 Blast Furnace Tap-Hole Refractory
- Dow Latex XZ 92219.00 Experimental Latex
- Barlog Plastics KEBATER BM240 PBT, 40% mineral reinforced, food grade
- Aclo Accutech Polypropylene Homopolymer HP0339T40L1 Talc Reinforced
- Ravago Manufacturing Americas Hylex® P1010G15 HB Polycarbonate, 15% Fiberglass Reinforced
Copyright © lookpolymers.com All Rights Reserved