Tipco Tipcofil® AGM 602 - 10% Mineral & 20% Glass Fiber Reinforced Nylon-6 Compound, with High Heat Stability
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | Tipco Industries Ltd., India |
| Trade Name | Tipcofil® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Tipco Tipcofil® AGM 602 - 10% Mineral & 20% Glass Fiber Reinforced Nylon-6 Compound, with High Heat Stability.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
10% Mineral + 20% Glass Reinforced Nylon-6 CompoundApplications: General PurposeProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd.,
India.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ASTM D792 |
| Water Absorption | 1.25 % | 1.25 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | ASTM D955 |
| Melt Flow | 10 g/10 min | 10 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 120 MPa | 17400 psi | ASTM D638 |
| Elongation at Break | >= 4.0 % | >= 4.0 % | ASTM D638 |
| Flexural Yield Strength | 160 MPa | 23200 psi | ASTM D790 |
| Flexural Modulus | 6.60 GPa | 957 ksi | ASTM D790 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | ASTM D256 |
| Izod Impact, Unnotched (ISO) | 50.0 kJ/m² | 23.8 ft-lb/in² | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | ASTM D648 |
| Vicat Softening Point | 210 °C | 410 °F | ASTM D1525 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 250 °C | 482 °F | |
| Rear Barrel Temperature | 240 °C | 464 °F | |
| Middle Barrel Temperature | 250 °C | 482 °F | |
| Front Barrel Temperature | 255 °C | 491 °F | |
| Nozzle Temperature | 250 °C | 482 °F | |
| Mold Temperature | 85.0 °C | 185 °F | |
| Drying Temperature | 85.0 °C | 185 °F |
Users viewing this material also viewed the following:
- SABIC M40060 Series High Density Polyethylene for Injection Molding
- DuPont Performance Polymers Zytel® 105F BK010 Nylon 66 (Unverified Data**)
- Karina SDB 35/3-LMP Ivory PVC Compound
- LATI Latilub 80-10T K/15 PPS, 15% Carbon Fiber Reinforced, PTFE Filled
- Solvay Specialty Polymers AvaSpire® AV-621 GF30 Polyaryletherketone (PAEK), 30% Glass Fiber
- SCG Chemicals EL-Leneâ„¢ M70 Butene (C4) Rotational Molding Resin
- Universal Wire Works Multimet (N-155) (AMS 5794) Filler Metal
- Hexcel® HexWeb® CR III 1/4-5052-.003 Corrosion Resistant Specification Grade Aluminum Honeycomb
- Total PPC 4720 WZ Polypropylene, Impact Copolymer
- Plastics Group Polifil® T-10 10% Talc-Reinforced Polypropylene
Copyright © lookpolymers.com All Rights Reserved