LG Chemical LUCON PO6063 mPPO+CNT+CF+GF
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, 10% Glass Filled |
| Manufacturer | LG Chemical |
| Trade Name | LUCON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUCON PO6063 mPPO+CNT+CF+GF.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding, mPPO+CNT+CF+GF, Electrostatic Dissipation, High Strength, Low WarpageApplication: LCD Cell TrayCAS No. 35134-01-4, 65997-17-3, 7440-44-0 and 7782-42-5Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.25 g/cc | 1.25 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm |
0.0010 - 0.0030 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 37 g/10 min @Load 10.0 kg, Temperature 300 °C |
37 g/10 min @Load 22.0 lb, Temperature 572 °F |
ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 98.1 MPa @Thickness 3.20 mm |
14200 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | >= 2.5 % @Thickness 3.20 mm |
>= 2.5 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 142 MPa @Thickness 3.20 mm |
20600 psi @Thickness 0.126 in |
15mm/min; ASTM D790 |
| Flexural Modulus | 9.51 GPa @Thickness 3.20 mm |
1380 ksi @Thickness 0.126 in |
15mm/min; ASTM D790 |
| Izod Impact, Notched | 0.588 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
1.10 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 131 °C @Thickness 6.40 mm |
268 °F @Thickness 0.252 in |
ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 10000 - 1.00e+6 ohm | 10000 - 1.00e+6 ohm | IEC 60093 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 270 - 290 °C | 518 - 554 °F | Injection Molding |
| Middle Barrel Temperature | 270 - 290 °C | 518 - 554 °F | Injection Molding |
| Front Barrel Temperature | 280 - 310 °C | 536 - 590 °F | Injection Molding |
| Nozzle Temperature | 280 - 300 °C | 536 - 572 °F | Injection Molding |
| Melt Temperature | 280 - 300 °C | 536 - 572 °F | Injection Molding |
| Mold Temperature | 90.0 - 120 °C | 194 - 248 °F | Injection Molding |
| Drying Temperature | 90.0 - 110 °C | 194 - 230 °F | Injection Molding |
| Dry Time | 4.00 - 5.00 hour | 4.00 - 5.00 hour | Injection Molding |
| Back Pressure | 0.000 - 1.96 MPa | 0.000 - 284 psi | Injection Molding |
| Screw Speed | 40 - 60 rpm | 40 - 60 rpm | Injection Molding |
Users viewing this material also viewed the following:
- Polymax® Maxelast® P2840 TPE, PP Overmold or Standalone use
- LG Chemical LUMID LW4403A(W) PA66+GF/MF40%, Low Warpage
- Inhance Fluoro-Seal INHANCE® HD-1035 HDPE
- Sinotek Materials WT88-45/75 Amorphous Graphite Powder
- E-Polymers TEKANATE™ G720 , 20% Glass Fiber Reinforced Poly Carbonate
- 3M Scotch® 3782 Performance Continuous Taping System Tape
- Beijing Ranger Chem SM-815CA Liquid Epoxy Resin
- Alliance N-40 Neodymium Iron Boron Magnetic Material
- Beijing Evergrow Resources ACFP-60 Activated Carbon Fiber Powder
Copyright © lookpolymers.com All Rights Reserved