LG Chemical LUCEL FW715CS Modified POM, Friction Resistance, Abrasion Resistance
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced |
| Manufacturer | LG Chemical |
| Trade Name | LUCEL |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUCEL FW715CS Modified POM, Friction Resistance, Abrasion Resistance.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Feature: Injection Molding, Modified POM, Friction Resistance, Abrasion ResistanceApplication: Gears, Printer Roller Pumps, Gear Worm WheelsCAS No. 66455-31-0 and 471-34-1Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.49 g/cc | 1.49 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.10 | 0.10 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.017 - 0.021 cm/cm @Thickness 3.20 mm |
0.017 - 0.021 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 10 g/10 min @Load 2.16 kg, Temperature 190 °C |
10 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 69 | 69 | ASTM D785 |
| Tensile Strength, Yield | 43.2 MPa @Thickness 3.20 mm |
6270 psi @Thickness 0.126 in |
5mm/min; ASTM D638 |
| Elongation at Break | 123 % @Thickness 3.20 mm |
123 % @Thickness 0.126 in |
5mm/min; ASTM D638 |
| Flexural Yield Strength | 64.7 MPa @Thickness 3.20 mm |
9390 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| Flexural Modulus | 1.9871 GPa @Thickness 3.20 mm |
288.21 ksi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| Izod Impact, Notched | 0.500 J/cm @Thickness 6.40 mm, Temperature 23.0 °C |
0.937 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C @Thickness 6.40 mm |
198 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Flammability, UL94 | HB @Thickness >=0.950 mm |
HB @Thickness >=0.0374 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 160 - 180 °C | 320 - 356 °F | Injection Molding |
| Middle Barrel Temperature | 170 - 190 °C | 338 - 374 °F | Injection Molding |
| Front Barrel Temperature | 180 - 200 °C | 356 - 392 °F | Injection Molding |
| Nozzle Temperature | 180 - 200 °C | 356 - 392 °F | Injection Molding |
| Melt Temperature | 200 - 220 °C | 392 - 428 °F | Injection Molding |
| Mold Temperature | 80.0 - 110 °C | 176 - 230 °F | Injection Molding |
| Drying Temperature | 90.0 - 110 °C | 194 - 230 °F | Injection Molding |
| Dry Time | 2.00 - 3.00 hour | 2.00 - 3.00 hour | Injection Molding |
| Back Pressure | 0.490 - 3.04 MPa | 71.1 - 441 psi | Injection Molding |
| Screw Speed | 50 - 100 rpm | 50 - 100 rpm | Injection Molding |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® IR2240 PC (Europe-Africa-Middle East)
- DuPont™ Biomax® 800C Hydro/Biodegradable Polyester (discontinued **)
- Dielectric Polymers NT-5513 High Tack Tape (discontinued **)
- Industeel URANUS® 35N 23.04 Duplex Stainless Steel with PREN = 24
- SABIC Innovative Plastics LNP THERMOCOMP MX99432 PP
- A. Schulman PP 1449-01 Polypropylene General-Purpose Homopolymer Polypropylene
- ChevronTexaco Multifak® EP NLGI Grade 2
- Arkema Group Pebax® 6333 SA 01 Polyether Block Amide (PEBA)
- BASF Ultramid® 8350 HS BK-102 PA6 (Dry)
- A. Schulman ComAlloy E-16822-1B Internally Lubricated, Carbon Fiber Reinforced Nylon 6/6
Copyright © lookpolymers.com All Rights Reserved