LATI Latiohm 87/28-05 PD01 G/10 PC, 10% Glass Fiber Reinforced
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 10% Glass Filled |
| Manufacturer | LATI |
| Trade Name | Latiohm |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LATI Latiohm 87/28-05 PD01 G/10 PC, 10% Glass Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Semiconductive/dissipative product based on Polycarbonate (PC). Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.28 g/cc | 0.0462 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0035 cm/cm | 0.0020 - 0.0035 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0035 - 0.0055 cm/cm | 0.0035 - 0.0055 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 100 MPa | 14500 psi | |
| Elongation at Break | 1.8 % | 1.8 % | |
| Tensile Modulus | 7.50 GPa | 1090 ksi | |
| Charpy Impact Unnotched | 3.50 J/cm² | 16.7 ft-lb/in² | |
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 145 °C | 293 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | |
| Vicat Softening Point | 150 °C @Load 5.00 kg |
302 °F @Load 11.0 lb |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 3000 ohm-cm | 3000 ohm-cm | |
| Surface Resistance | 2000 ohm | 2000 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 275 - 320 °C | 527 - 608 °F | |
| Mold Temperature | 100 - 120 °C | 212 - 248 °F | |
| Drying Temperature | 110 - 130 °C @Time 10800 sec |
230 - 266 °F @Time 3.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shrinkage - Pressure | 60 MPa |
Users viewing this material also viewed the following:
- Process Technologies Inc Viton®/FKM Sanitary Gasket
- Parabeam Industrie Paraglass 12 3D Glass Fabric
- Industrial Nanotech Nansulateâ„¢ High Heat Translucent Insulation Coating
- Ineos H02C-00 Polypropylene Homopolymer
- Lehmann & Voss LUVOCOM® 1/GF/20/TF/10/SI/2/BK Polyamide 66, with glass fiber, PTFE, lubricant modified
- A. Schulman PP 2175 Polypropylene High Flow Copolymer Polypropylene
- Master Bond Supreme 11 High Peel and Shear Strength Epoxy Adhesive
- Covestro Makrolon® GF9002* Polycarbonate, 10% Glass Filled
- BNZ Materials Bazelite 2600 LI Insulating Castable
Copyright © lookpolymers.com All Rights Reserved