LATI Latimass 52/11-01 D020 PP Homopolymer

Category Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer LATI
Trade Name Latimass
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latimass 52/11-01 D020 PP Homopolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Specific density compound based on Polypropylene homopolymer (PPh). Special filler. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 2.05 g/cc
0.0741 lb/in³
Linear Mold Shrinkage, Flow 0.012 - 0.015 cm/cm
0.012 - 0.015 in/in
Linear Mold Shrinkage, Transverse 0.0125 - 0.0155 cm/cm
0.0125 - 0.0155 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 15.0 MPa
2180 psi
Elongation at Break 1.0 %
1.0 %
Tensile Modulus 2.90 GPa
421 ksi
Charpy Impact Unnotched 1.00 J/cm²
4.76 ft-lb/in²
Charpy Impact, Notched 0.130 J/cm²
0.619 ft-lb/in²
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 95.0 °C
203 °F
Deflection Temperature at 1.8 MPa (264 psi) 65.0 °C
149 °F
Vicat Softening Point 95.0 °C

@Load 5.00 kg
203 °F

@Load 11.0 lb
Processing Properties Metric English Comments
Melt Temperature 190 - 220 °C
374 - 428 °F
Mold Temperature 50.0 - 70.0 °C
122 - 158 °F
Drying Temperature 80.0 - 90.0 °C

@Time 10800 sec
176 - 194 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa