LATI Latilub 87/28-17ST K/15 PC, 15% Carbon Fiber Reinforced, Silicone/PTFE Filled

Category	Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Carbon + PTFE Filled
Manufacturer	LATI
Trade Name	Latilub
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LATI Latilub 87/28-17ST K/15 PC, 15% Carbon Fiber Reinforced, Silicone/PTFE Filled.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Self-lubricating product based on Polycarbonate (PC). Silicone / PTFE. Carbon fiber. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.

Physical Properties	Metric	English
Density	1.33 g/cc	0.0480 lb/inÂ³
Linear Mold Shrinkage, Flow	0.0020 - 0.0030 cm/cm	0.0020 - 0.0030 in/in
Linear Mold Shrinkage, Transverse	0.0030 - 0.0050 cm/cm	0.0030 - 0.0050 in/in

Mechanical Properties	Metric	English
Tensile Strength at Break	105 MPa	15200 psi
Elongation at Break	2.0 %	2.0 %
Tensile Modulus	10.5 GPa	1520 ksi
Charpy Impact Unnotched	3.00 J/cmÂ²	14.3 ft-lb/inÂ²
Charpy Impact, Notched	0.800 J/cmÂ²	3.81 ft-lb/inÂ²
Coefficient of Friction, Dynamic	0.16	0.16
Coefficient of Friction, Static	0.22	0.22
K (wear) Factor	7.00 x 10^-8 mmÂ³/N-M	3.47 x 10^-10 inÂ³-min/ft-lb-hr

Thermal Properties	Metric	English
Deflection Temperature at 0.46 MPa (66 psi)	145 Â°C	293 Â°F
Deflection Temperature at 1.8 MPa (264 psi)	140 Â°C	284 Â°F
Vicat Softening Point	150 Â°C @Load 5.00 kg	302 Â°F @Load 11.0 lb

Electrical Properties	Metric	English	Comments
Volume Resistivity	450 ohm-cm	450 ohm-cm
Surface Resistance	250 ohm	250 ohm

Processing Properties	Metric	English
Melt Temperature	275 - 320 Â°C	527 - 608 Â°F
Mold Temperature	80.0 - 110 Â°C	176 - 230 Â°F
Drying Temperature	110 - 130 Â°C @Time 10800 sec	230 - 266 Â°F @Time 3.00 hour

Descriptive Properties	Value	Comments
ISO Shrinkage - Pressure	60 MPa