LATI Latilub 75/4-20T PBT, PTFE Filled

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), PTFE Filled
Manufacturer LATI
Trade Name Latilub
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latilub 75/4-20T PBT, PTFE Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Self-lubricating product based on Polybutylene Terephthalate (PBT). PTFE.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.41 g/cc
0.0509 lb/in³
Linear Mold Shrinkage, Flow 0.018 - 0.021 cm/cm
0.018 - 0.021 in/in
Linear Mold Shrinkage, Transverse 0.018 - 0.0205 cm/cm
0.018 - 0.0205 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 40.0 MPa
5800 psi
Elongation at Break 8.0 %
8.0 %
Elongation at Yield 4.0 %
4.0 %
Tensile Modulus 2.30 GPa
334 ksi
Charpy Impact Unnotched 2.50 J/cm²
11.9 ft-lb/in²
Charpy Impact, Notched 0.150 J/cm²
0.714 ft-lb/in²
Coefficient of Friction, Dynamic 0.12
0.12
Coefficient of Friction, Static 0.15
0.15
K (wear) Factor 4.00 x 10-8 mm³/N-M
1.99 x 10-10 in³-min/ft-lb-hr
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 160 °C
320 °F
Deflection Temperature at 1.8 MPa (264 psi) 70.0 °C
158 °F
Vicat Softening Point 170 °C

@Load 5.00 kg
338 °F

@Load 11.0 lb
Processing Properties Metric English Comments
Melt Temperature 230 - 245 °C
446 - 473 °F
Mold Temperature 70.0 - 90.0 °C
158 - 194 °F
Drying Temperature 100 - 120 °C

@Time 10800 sec
212 - 248 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa