LATI Latilon 28D G/30 PC, 30% Glass Fiber Reinforced

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 30% Glass Filled
Manufacturer LATI
Trade Name Latilon
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latilon 28D G/30 PC, 30% Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polycarbonate (PC) based compound. Glass fibers. Low smoke density and low toxicity index. High dimensional stability.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.44 g/cc
0.0520 lb/in³
Linear Mold Shrinkage, Flow 0.0015 - 0.0035 cm/cm
0.0015 - 0.0035 in/in
Linear Mold Shrinkage, Transverse 0.0035 - 0.0055 cm/cm
0.0035 - 0.0055 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 50.0 MPa

@Temperature 120 °C
7250 psi

@Temperature 248 °F
70.0 MPa

@Temperature 90.0 °C
10200 psi

@Temperature 194 °F
80.0 MPa

@Temperature 60.0 °C
11600 psi

@Temperature 140 °F
90.0 MPa

@Temperature 23.0 °C
13100 psi

@Temperature 73.4 °F
Elongation at Break 1.4 %

@Temperature 60.0 °C
1.4 %

@Temperature 140 °F
1.5 %

@Temperature 90.0 °C
1.5 %

@Temperature 194 °F
1.5 %

@Temperature 120 °C
1.5 %

@Temperature 248 °F
1.7 %

@Temperature 23.0 °C
1.7 %

@Temperature 73.4 °F
Tensile Modulus 6.20 GPa

@Temperature 120 °C
899 ksi

@Temperature 248 °F
7.00 GPa

@Temperature 90.0 °C
1020 ksi

@Temperature 194 °F
7.50 GPa

@Temperature 60.0 °C
1090 ksi

@Temperature 140 °F
8.00 GPa

@Temperature 23.0 °C
1160 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 3.20 J/cm²

@Temperature -20.0 °C
15.2 ft-lb/in²

@Temperature -4.00 °F
4.00 J/cm²

@Temperature 23.0 °C
19.0 ft-lb/in²

@Temperature 73.4 °F
Charpy Impact, Notched 0.680 J/cm²

@Temperature -20.0 °C
3.24 ft-lb/in²

@Temperature -4.00 °F
1.00 J/cm²

@Temperature 23.0 °C
4.76 ft-lb/in²

@Temperature 73.4 °F
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 135 °C
275 °F
Deflection Temperature at 0.46 MPa (66 psi) 140 °C
284 °F
Deflection Temperature at 1.8 MPa (264 psi) 135 °C
275 °F
Vicat Softening Point 145 °C

@Load 5.00 kg
293 °F

@Load 11.0 lb
Flammability, UL94 V-1

@Thickness 1.50 mm
V-1

@Thickness 0.0591 in
Oxygen Index 31 %
31 %
Electrical Properties Metric English Comments
Comparative Tracking Index 150 V
150 V
A solution
Processing Properties Metric English Comments
Melt Temperature 280 - 300 °C
536 - 572 °F
Mold Temperature 100 - 120 °C
212 - 248 °F
Drying Temperature 120 - 130 °C

@Time 10800 sec
248 - 266 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa