LATI Latamid 66 H2 K/50 PA 66, 50% Carbon Fiber Reinforced, Heat Stabilized

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 50% Carbon Fiber Filled
Manufacturer LATI
Trade Name Latamid
Port Shanghai port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF LATI Latamid 66 H2 K/50 PA 66, 50% Carbon Fiber Reinforced, Heat Stabilized.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Polyamide 66 (PA66) based compound. Heat stabilized. Carbon fiber.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.37 g/cc
0.0495 lb/in³
Linear Mold Shrinkage, Flow 0.0010 - 0.0030 cm/cm
0.0010 - 0.0030 in/in
Linear Mold Shrinkage, Transverse 0.0035 - 0.0055 cm/cm
0.0035 - 0.0055 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 100 MPa
<br>@Temperature 150 °C
 14500 psi
<br>@Temperature 302 °F
125 MPa
<br>@Temperature 120 °C
 18100 psi
<br>@Temperature 248 °F
140 MPa
<br>@Temperature 90.0 °C
 20300 psi
<br>@Temperature 194 °F
170 MPa
<br>@Temperature 60.0 °C
 24700 psi
<br>@Temperature 140 °F
210 MPa
<br>@Temperature 23.0 °C
 30500 psi
<br>@Temperature 73.4 °F
Elongation at Break 1.0 %
<br>@Temperature 23.0 °C
 1.0 %
<br>@Temperature 73.4 °F
1.5 %
<br>@Temperature 60.0 °C
 1.5 %
<br>@Temperature 140 °F
2.4 %
<br>@Temperature 90.0 °C
 2.4 %
<br>@Temperature 194 °F
2.8 %
<br>@Temperature 120 °C
 2.8 %
<br>@Temperature 248 °F
2.9 %
<br>@Temperature 150 °C
 2.9 %
<br>@Temperature 302 °F
Tensile Modulus 9.50 GPa
<br>@Temperature 150 °C
 1380 ksi
<br>@Temperature 302 °F
12.0 GPa
<br>@Temperature 120 °C
 1740 ksi
<br>@Temperature 248 °F
17.5 GPa
<br>@Temperature 90.0 °C
 2540 ksi
<br>@Temperature 194 °F
27.0 GPa
<br>@Temperature 60.0 °C
 3920 ksi
<br>@Temperature 140 °F
29.0 GPa
<br>@Temperature 23.0 °C
 4210 ksi
<br>@Temperature 73.4 °F
Charpy Impact Unnotched 3.50 J/cm²
16.7 ft-lb/in²
Charpy Impact, Notched 0.700 J/cm²
3.33 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 135 °C
275 °F
Deflection Temperature at 0.46 MPa (66 psi) 260 °C
500 °F
Deflection Temperature at 1.8 MPa (264 psi) 250 °C
482 °F
Vicat Softening Point 250 °C
<br>@Load 5.00 kg
 482 °F
<br>@Load 11.0 lb
Electrical Properties Metric English Comments
Volume Resistivity 50 ohm-cm
50 ohm-cm
Surface Resistance 10 ohm
10 ohm
Processing Properties Metric English Comments
Melt Temperature 280 - 310 °C
536 - 590 °F
Mold Temperature 80.0 - 100 °C
176 - 212 °F
Drying Temperature 90.0 - 100 °C
<br>@Time 10800 sec
 194 - 212 °F
<br>@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa