LATI Latamid 66 H2 G/25-V0KB1 PA 66, 25% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled , Nylon 66, Glass Fiber Filled, Flame Retardant
Manufacturer LATI
Trade Name Latamid
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latamid 66 H2 G/25-V0KB1 PA 66, 25% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyamide 66 (PA66) based compound. Heat stabilized. Glass fibers. UL94 V-0 classified, with red phosphorous. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.32 g/cc
0.0477 lb/in³
Linear Mold Shrinkage, Flow 0.0035 - 0.0065 cm/cm
0.0035 - 0.0065 in/in
Linear Mold Shrinkage, Transverse 0.0075 - 0.0105 cm/cm
0.0075 - 0.0105 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 55.0 MPa

@Temperature 150 °C
 7980 psi

@Temperature 302 °F
65.0 MPa

@Temperature 120 °C
 9430 psi

@Temperature 248 °F
80.0 MPa

@Temperature 90.0 °C
 11600 psi

@Temperature 194 °F
115 MPa

@Temperature 60.0 °C
 16700 psi

@Temperature 140 °F
145 MPa

@Temperature 23.0 °C
 21000 psi

@Temperature 73.4 °F
Elongation at Break 3.1 %

@Temperature 23.0 °C
 3.1 %

@Temperature 73.4 °F
3.8 %

@Temperature 60.0 °C
 3.8 %

@Temperature 140 °F
5.2 %

@Temperature 90.0 °C
 5.2 %

@Temperature 194 °F
5.7 %

@Temperature 120 °C
 5.7 %

@Temperature 248 °F
6.0 %

@Temperature 150 °C
 6.0 %

@Temperature 302 °F
Elongation at Yield 4.5 %

@Temperature 90.0 °C
 4.5 %

@Temperature 194 °F
4.8 %

@Temperature 120 °C
 4.8 %

@Temperature 248 °F
5.5 %

@Temperature 150 °C
 5.5 %

@Temperature 302 °F
Tensile Modulus 0.330 GPa

@Temperature 150 °C
 47.9 ksi

@Temperature 302 °F
4.00 GPa

@Temperature 120 °C
 580 ksi

@Temperature 248 °F
4.80 GPa

@Temperature 90.0 °C
 696 ksi

@Temperature 194 °F
7.30 GPa

@Temperature 60.0 °C
 1060 ksi

@Temperature 140 °F
8.40 GPa

@Temperature 23.0 °C
 1220 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 5.50 J/cm²
26.2 ft-lb/in²
Charpy Impact, Notched 0.800 J/cm²
3.81 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 125 °C
257 °F
Deflection Temperature at 0.46 MPa (66 psi) 255 °C
491 °F
Deflection Temperature at 1.8 MPa (264 psi) 235 °C
455 °F
Vicat Softening Point 245 °C

@Load 5.00 kg
 473 °F

@Load 11.0 lb
Flammability, UL94 HB

@Thickness 0.750 mm
 HB

@Thickness 0.0295 in
V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
Oxygen Index 27 %
27 %
Glow Wire Test 750 °C

@Thickness 1.00 mm
 1380 °F

@Thickness 0.0394 in
 GWIT
750 °C

@Thickness 2.00 mm
 1380 °F

@Thickness 0.0787 in
 GWIT
960 °C

@Thickness 1.00 mm
 1760 °F

@Thickness 0.0394 in
 GWFI/GWT
960 °C

@Thickness 2.00 mm
 1760 °F

@Thickness 0.0787 in
 GWFI/GWT
Electrical Properties Metric English Comments
Comparative Tracking Index 400 V
400 V
A solution
Processing Properties Metric English Comments
Melt Temperature 270 - 290 °C
518 - 554 °F
Mold Temperature 70.0 - 100 °C
158 - 212 °F
Drying Temperature 90.0 - 100 °C

@Time 10800 sec
 194 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa