LATI Latamid 6 H2 G/50 PA 6, 50% Glass Fiber Reinforced, Heat Stabilized

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 50% Glass Fiber Filled
Manufacturer LATI
Trade Name Latamid
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latamid 6 H2 G/50 PA 6, 50% Glass Fiber Reinforced, Heat Stabilized.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyamide 6 (PA6) based compound. Heat stabilized. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.56 g/cc
0.0564 lb/in³
Linear Mold Shrinkage, Flow 0.0025 - 0.0045 cm/cm
0.0025 - 0.0045 in/in
Linear Mold Shrinkage, Transverse 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 100 MPa

@Temperature 150 °C
 14500 psi

@Temperature 302 °F
115 MPa

@Temperature 120 °C
 16700 psi

@Temperature 248 °F
130 MPa

@Temperature 90.0 °C
 18900 psi

@Temperature 194 °F
160 MPa

@Temperature 60.0 °C
 23200 psi

@Temperature 140 °F
215 MPa

@Temperature 23.0 °C
 31200 psi

@Temperature 73.4 °F
Elongation at Break 2.5 %

@Temperature 23.0 °C
 2.5 %

@Temperature 73.4 °F
3.0 %

@Temperature 60.0 °C
 3.0 %

@Temperature 140 °F
3.8 %

@Temperature 90.0 °C
 3.8 %

@Temperature 194 °F
4.5 %

@Temperature 120 °C
 4.5 %

@Temperature 248 °F
4.5 %

@Temperature 150 °C
 4.5 %

@Temperature 302 °F
Tensile Modulus 6.00 GPa

@Temperature 150 °C
 870 ksi

@Temperature 302 °F
6.90 GPa

@Temperature 120 °C
 1000 ksi

@Temperature 248 °F
8.50 GPa

@Temperature 90.0 °C
 1230 ksi

@Temperature 194 °F
12.5 GPa

@Temperature 60.0 °C
 1810 ksi

@Temperature 140 °F
15.5 GPa

@Temperature 23.0 °C
 2250 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 8.50 J/cm²
40.4 ft-lb/in²
Charpy Impact, Notched 1.50 J/cm²
7.14 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 130 °C
266 °F
Deflection Temperature at 0.46 MPa (66 psi) 225 °C
437 °F
Deflection Temperature at 1.8 MPa (264 psi) 215 °C
419 °F
Vicat Softening Point 220 °C

@Load 5.00 kg
 428 °F

@Load 11.0 lb
Flammability, UL94 HB

@Thickness 3.00 mm
 HB

@Thickness 0.118 in
HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
HB

@Thickness 0.750 mm
 HB

@Thickness 0.0295 in
Oxygen Index 25 %
25 %
Processing Properties Metric English Comments
Melt Temperature 240 - 280 °C
464 - 536 °F
Mold Temperature 80.0 - 100 °C
176 - 212 °F
Drying Temperature 90.0 - 100 °C

@Time 10800 sec
 194 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa