LATI Larton L G/40 L-PPS, 40% Glass Fiber Reinforced

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with 40% Glass Fiber Filler
Manufacturer LATI
Trade Name Larton
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Larton L G/40 L-PPS, 40% Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Linear Polyphenylene Sulfide (L-PPS) based compound. Glass fibers. Very good chemical resistance. Very good thermal properties. Low smoke density and low toxicity index.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.65 g/cc
0.0596 lb/in³
Linear Mold Shrinkage, Flow 0.0025 - 0.0040 cm/cm
0.0025 - 0.0040 in/in
Linear Mold Shrinkage, Transverse 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 70.0 MPa

@Temperature 150 °C
 10200 psi

@Temperature 302 °F
90.0 MPa

@Temperature 120 °C
 13100 psi

@Temperature 248 °F
120 MPa

@Temperature 90.0 °C
 17400 psi

@Temperature 194 °F
140 MPa

@Temperature 60.0 °C
 20300 psi

@Temperature 140 °F
160 MPa

@Temperature 23.0 °C
 23200 psi

@Temperature 73.4 °F
Elongation at Break 1.2 %

@Temperature 23.0 °C
 1.2 %

@Temperature 73.4 °F
1.3 %

@Temperature 60.0 °C
 1.3 %

@Temperature 140 °F
1.8 %

@Temperature 90.0 °C
 1.8 %

@Temperature 194 °F
2.2 %

@Temperature 120 °C
 2.2 %

@Temperature 248 °F
2.5 %

@Temperature 150 °C
 2.5 %

@Temperature 302 °F
Tensile Modulus 7.20 GPa

@Temperature 150 °C
 1040 ksi

@Temperature 302 °F
8.40 GPa

@Temperature 120 °C
 1220 ksi

@Temperature 248 °F
12.2 GPa

@Temperature 90.0 °C
 1770 ksi

@Temperature 194 °F
14.8 GPa

@Temperature 60.0 °C
 2150 ksi

@Temperature 140 °F
17.0 GPa

@Temperature 23.0 °C
 2470 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 3.00 J/cm²
14.3 ft-lb/in²
Charpy Impact, Notched 0.800 J/cm²
3.81 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 200 °C
392 °F
Deflection Temperature at 0.46 MPa (66 psi) 280 °C
536 °F
Deflection Temperature at 1.8 MPa (264 psi) 270 °C
518 °F
Vicat Softening Point 255 °C

@Load 5.00 kg
 491 °F

@Load 11.0 lb
Flammability, UL94 V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
V-0

@Thickness 0.750 mm
 V-0

@Thickness 0.0295 in
Processing Properties Metric English Comments
Melt Temperature 290 - 310 °C
554 - 590 °F
Mold Temperature 130 - 140 °C
266 - 284 °F
Drying Temperature 130 - 150 °C

@Time 10800 sec
 266 - 302 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa