LATI Kelon® B H CER/30 PA 6, 30% Mineral Reinforced, Heat Stabilized
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Mineral Filled |
| Manufacturer | LATI |
| Trade Name | Kelon® B |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LATI Kelon® B H CER/30 PA 6, 30% Mineral Reinforced, Heat Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polyamide 6 (PA6) based compound. Heat stabilized. Mineral filler. Very high dimensional stability. Good elongation.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.010 - 0.0125 cm/cm | 0.010 - 0.0125 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0105 - 0.0135 cm/cm | 0.0105 - 0.0135 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 20.0 MPa @Temperature 150 °C |
2900 psi @Temperature 302 °F |
|
| 25.0 MPa @Temperature 120 °C |
3630 psi @Temperature 248 °F |
||
| 35.0 MPa @Temperature 90.0 °C |
5080 psi @Temperature 194 °F |
||
| 45.0 MPa @Temperature 60.0 °C |
6530 psi @Temperature 140 °F |
||
| 80.0 MPa @Temperature 23.0 °C |
11600 psi @Temperature 73.4 °F |
||
| Elongation at Break | 3.5 % @Temperature 23.0 °C |
3.5 % @Temperature 73.4 °F |
|
| 4.5 % @Temperature 60.0 °C |
4.5 % @Temperature 140 °F |
||
| 10 % @Temperature 90.0 °C |
10 % @Temperature 194 °F |
||
| 20 % @Temperature 120 °C |
20 % @Temperature 248 °F |
||
| 35 % @Temperature 150 °C |
35 % @Temperature 302 °F |
||
| Tensile Modulus | 1.10 GPa @Temperature 150 °C |
160 ksi @Temperature 302 °F |
|
| 1.60 GPa @Temperature 120 °C |
232 ksi @Temperature 248 °F |
||
| 1.90 GPa @Temperature 90.0 °C |
276 ksi @Temperature 194 °F |
||
| 3.00 GPa @Temperature 60.0 °C |
435 ksi @Temperature 140 °F |
||
| 4.90 GPa @Temperature 23.0 °C |
711 ksi @Temperature 73.4 °F |
||
| Charpy Impact Unnotched | 3.00 J/cm² | 14.3 ft-lb/in² | |
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 125 °C | 257 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | |
| Vicat Softening Point | 210 °C @Load 5.00 kg |
410 °F @Load 11.0 lb |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 240 - 290 °C | 464 - 554 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |
| Drying Temperature | 90.0 - 100 °C @Time 10800 sec |
194 - 212 °F @Time 3.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shrinkage - Pressure | 60 MPa |
Users viewing this material also viewed the following:
- Nilit FRIANYL B63 AL40 Nylon 6.6 for injection molding, 40% aluminum filled
- PolyOne Geon™ Vinyl Flexible R7545H Polyvinyl Chloride, Flexible (PVC, Flexible)
- Solvay GEROPON® HW 15 Surfactant
- SABIC Innovative Plastics NORYL GTX GTX914 PPE+PA (Europe-Africa-Middle East)
- Struktol VM 512 LUBRICANT ADDITIVE FOR PVC AND POLYMER PROCESSING
- Wellman Wellpet® PR109-N1 Unfilled PET
- A. Schulman CP808-01 Natural Linear, Low-Density Polyethylene
- Daikin DAI-EL G-902 Fluoroelastomer Terpolymer, Peroxide Curable Grade, 71% Fluorine Content
- Kazanorgsintez PE2NT 11-285 High Density Polyethylene Composite
Copyright © lookpolymers.com All Rights Reserved