- Kuraray Genestarâ„¢ G1352A-M41 Nylon, 35% Glass Filled
Kuraray Genestarâ„¢ G1352A-M41 Nylon, 35% Glass Filled
| Category | Polymer , Thermoplastic , Nylon |
| Manufacturer | Kuraray Company |
| Trade Name | Genestar™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kuraray Genestarâ„¢ G1352A-M41 Nylon, 35% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Low friction reinforced injection grade.Main Features:Low friction coefficientAbrasion resistanceExamples of applications:Friction and wear applicationGear and wheel
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.50 g/cc | 1.50 g/cc | |
| Density | 1.50 g/cc | 0.0542 lb/in³ | ISO 1183 |
| Water Absorption | 0.14 % | 0.14 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | ISO 294-4, 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 200 MPa | 29000 psi | ISO 527-1/-2 |
| Elongation at Break | 2.5 % | 2.5 % | ISO 527-1/-2 |
| Tensile Modulus | 11.6 GPa | 1680 ksi | ISO 527-1/-2 |
| Flexural Strength | 290 MPa | 42100 psi | ISO 178 |
| Flexural Modulus | 10.7 GPa | 1550 ksi | ISO 178 |
| Charpy Impact, Notched | 1.30 J/cm² | 6.19 ft-lb/in² | ISO 179/1eA |
| Coefficient of Friction | 0.30 | 0.30 | ISO JIS K7218-A |
| K Factor (Wear Factor) | 10 | 10 | [mg] |
| Limiting Pressure Velocity | 1.50 MPa-m/sec | 42800 psi-ft/min |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 17.0 µm/m-°C | 9.44 µin/in-°F | ASTM D696 |
| CTE, linear, Transverse to Flow | 45.0 µm/m-°C | 25.0 µin/in-°F | ASTM D696 |
| Melting Point | 300 °C | 572 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 270 °C | 518 °F | ISO 75-1/-2 |
| Glass Transition Temp, Tg | 125 °C | 257 °F | 10°C/min; ISO 11357-1/-2 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additives | Lubricants | |
| Release Agent | ||
| Applications | Automotive | |
| General Purpose | ||
| Chemical Resistance | Acid Resistance | |
| Alkali Resistance | ||
| Environmental Stress Crack Resistance | ||
| General Chemical Resistance | ||
| Grease Resistance | ||
| Hydrolytically Stable | ||
| Oil Resistance | ||
| Solvent Resistance | ||
| Delivery Form | Black | |
| Other Features | Barrier Properties | |
| Creep Resistance | ||
| High Crystalinity | ||
| Low Coefficient of Friction | ||
| Thermal Stability | ||
| Weldable | ||
| Regional Availability | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America | ||
| Special Characteristics | Heat Stabilized or Stable to Heat |
Users viewing this material also viewed the following:
- LyondellBasell Alathon® H6018 High Density Polyethylene (Extrusion Grade)
- Michelman® ThermaGloss® 419 Water based over print varnish
- SABIC Innovative Plastics LNP LUBRILOY D2000P PC (Asia Pacific)
- SABIC Innovative Plastics Valox® IQ357 PBT+PC
- A. Schulman POLYFORT™ FPP 1285 Glass Fiber-Reinforced Copolymer Polypropylene
- ChevronTexaco Regal® 460 R&O
- BASF Ultramid® A3HG7 BK 00564 35% Glass Filled PA66 (Conditioned)
- 3M Scotchlite™ 680CR-64 Removable Reflective Graphic Film with Comply™ Adhesive
- Bostik 2107 General Purpose EVA Glue Stick
- Solvay MIRACARE® BT Surfactant
Copyright © lookpolymers.com All Rights Reserved