Kuraray Genestarâ„¢ G1350A-M42 Nylon, 35% Glass Filled

Category Polymer , Thermoplastic , Nylon
Manufacturer Kuraray Company
Trade Name Genestar™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Kuraray Genestarâ„¢ G1350A-M42 Nylon, 35% Glass Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
35% Glass reinforced injection grade. This grade was developed specifically for improved performance in a 50/50 ethylene glycol and water environment.Main Features:Hydrolysis resistanceHeat resistanceChemical resistanceExamples of applications:Thermostat housingsWater inlets, outlets, and valves
Physical Properties Metric English Comments
Specific Gravity 1.40 g/cc
1.40 g/cc
Density 1.58 g/cc
0.0571 lb/in³
ISO 1183
Water Absorption 0.19 %
0.19 %
ISO 62
Linear Mold Shrinkage, Flow 0.0030 cm/cm
0.0030 in/in
ISO 294-4, 2577
Linear Mold Shrinkage, Transverse 0.0090 cm/cm
0.0090 in/in
ISO 294-4, 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 200 MPa
29000 psi
ISO 527-1/-2
Elongation at Break 2.5 %
2.5 %
ISO 527-1/-2
Tensile Modulus 11.0 GPa
1600 ksi
ISO 527-1/-2
Flexural Strength 285 MPa
41300 psi
ISO 178
Flexural Modulus 10.0 GPa
1450 ksi
ISO 178
Charpy Impact, Notched 1.20 J/cm²
5.71 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 19.0 µm/m-°C
10.6 µin/in-°F
ASTM D696
CTE, linear, Transverse to Flow 39.0 µm/m-°C
21.7 µin/in-°F
ASTM D696
Melting Point 300 °C
572 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 1.8 MPa (264 psi) 270 °C
518 °F
ISO 75-1/-2
Glass Transition Temp, Tg 125 °C
257 °F
10°C/min; ISO 11357-1/-2
Descriptive Properties Value Comments
Additives Release Agent
Applications Automotive
General Purpose
Chemical Resistance Acid Resistance
Alkali Resistance
Environmental Stress Crack Resistance
General Chemical Resistance
Grease Resistance
Hydrolytically Stable
Oil Resistance
Solvent Resistance
Delivery Form Black
Other Features Barrier Properties
Creep Resistance
High Crystalinity
Thermal Stability
Weldable
Regional Availability Asia Pacific
Europe
Near East/Africa
North America
South and Central America
Special Characteristics Heat Stabilized or Stable to Heat