SABIC Innovative Plastics LNP THERMOCOMP DF004P PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP DF004P PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* DF004P is a compound based on Polycarbonate resin containing 20% Glass Fiber. Added features of this material include: Exceptional Processing.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.34 g/cc | 1.34 g/cc | ASTM D792 |
| Moisture Absorption | 0.120 % | 0.120 % | 50% RH, 24 hrs; ASTM D570 |
| 0.190 % | 0.190 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Time 86400 sec |
0.0020 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0023 cm/cm @Time 86400 sec |
0.0023 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0067 cm/cm @Time 86400 sec |
0.0067 in/in @Time 24.0 hour |
ISO 294 |
| 0.0070 cm/cm @Time 86400 sec |
0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 102 MPa | 14800 psi | ISO 527 |
| 104 MPa | 15100 psi | ASTM D638 | |
| Elongation at Break | 3.2 % | 3.2 % | ASTM D638 |
| 3.2 % | 3.2 % | ISO 527 | |
| Tensile Modulus | 6.05 GPa | 877 ksi | 1 mm/min; ISO 527 |
| 6.19 GPa | 898 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 162 MPa | 23500 psi | ISO 178 |
| 172 MPa | 24900 psi | ASTM D790 | |
| Flexural Modulus | 5.99 GPa | 869 ksi | ISO 178 |
| 6.17 GPa | 895 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.740 J/cm | 1.39 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.10 J/cm | 13.3 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 48.0 kJ/m² | 22.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 8.00 J | 5.90 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 33.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
18.6 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 33.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
18.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 54.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
30.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 68.9 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 139 °C | 282 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 138 °C @Thickness 3.20 mm |
280 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Owens Corning Glass Fiber Reinforced Polyester BMC (Injection), 22 wt.% glass
- SABIC Innovative Plastics Lexan® EXL6414 PC (Europe-Africa-Middle East)
- Phillips 66 COPYLENE® CM100LN Polypropylene, Impact Copolymer, Medium Impact, Nucleated, Antistat, Injection Molding
- Kazanorgsintez Synthanox 1720-9
- Momentive Performance Materials HPC Boron Nitride (BN)/TiO2 Water Based Coating
- SABIC Innovative Plastics LNP LUBRICOMP EFL36 PEI (Europe-Africa-Middle East)
- Universal Wire Works BAu-5 (AMS 4785) Gold Brazing Filler Metal
- A. Schulman POLYFORT™ FPP 2388 Glass Reinforced Polypropylene
- ExxonMobil Label-Lyte™ 65LT500 OPP Film
Copyright © lookpolymers.com All Rights Reserved