Kolon SPESIN® KP213G15SIBL Glass Fiber Reinforced PBT Compound Resin
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled |
| Manufacturer | Kolon |
| Trade Name | SPESIN® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kolon SPESIN® KP213G15SIBL Glass Fiber Reinforced PBT Compound Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
G/F 15%, high toughness, excellent surfaceApplications: Various types of housingsInformation provided by API-Kolon.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.41 g/cc | 1.41 g/cc | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.050 % | 0.050 % | 60% RH; ASTM D570 |
| Linear Mold Shrinkage | 0.0070 - 0.011 cm/cm | 0.0070 - 0.011 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength | 103 MPa | 14900 psi | ASTM D638 |
| Elongation at Break | 7.0 % | 7.0 % | ASTM D638 |
| Flexural Strength | 172 MPa | 24900 psi | ASTM D790 |
| Flexural Modulus | 5.394 GPa | 782.3 ksi | ASTM D790 |
| Izod Impact, Notched | 0.490 J/cm | 0.918 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 40.0 µm/m-°C | 22.2 µin/in-°F | ASTM D696 |
| Melting Point | 224 °C | 435 °F | ASTM D1525 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.2 | 3.2 | ASTM D150 |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | ASTM D149 |
| Arc Resistance | 120 sec | 120 sec | ASTM D495 |
Users viewing this material also viewed the following:
- Nye Lubricants 748 (RL) Synthetic Oil
- Resinoid 2215 Phenolic Molding, Cellulose Reinforced
- MarkeTech Zirconium Oxide Ceramic - Zirconia, Y2O3 Stabilized
- Kolon KOPA® KN333MT30BL Mineral Reinforced Nylon 66
- Teknor Apex Monprene® MP-1672A Thermoplastic Elastomer
- Plenco 7500 Phenolic, Granular, Injection Molded
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer with 10 PHR Tricresyl Phosphate
- ATI Allvac® 6-6-2 Titanium Alloy, Heat Treatment: 718°C (1325°F) Anneal
- Trelleborg Commercial Neoprene® C500 Chloroprene
- A. Schulman POLYBATCH™ Woodland Green 30233U/4 Concentrate Based In LLDPE
Copyright © lookpolymers.com All Rights Reserved