Kolon KOPA® KN333MS Low Friction Nylon 66

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer Kolon
Trade Name Kopa®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Kolon KOPA® KN333MS Low Friction Nylon 66.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in the automobile, electrical and industrial parts.High tensile strength, outstanding self lubrication and abrasion resistance, excellent chemical & weather resistance, high usage temperatureInformation provided by US distributor, API-Kolon.
Physical Properties Metric English Comments
Density 1.16 g/cc
0.0419 lb/in³
DIN 53479; ASTM D792
Water Absorption 1.0 %
1.0 %
DIN 53475; ASTM D570
Linear Mold Shrinkage 0.010 - 0.012 cm/cm
0.010 - 0.012 in/in
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell R 125
125
DIN 53505; ASTM D785
Tensile Strength, Ultimate 93.2 MPa
13500 psi
DIN 53455; ASTM D638
Elongation at Break 10 %
10 %
DIN 53455; ASTM D638
Flexural Yield Strength 123 MPa
17800 psi
DIN 53455; ASTM D790
Flexural Modulus 2.89 GPa
420 ksi
DIN 53452; ASTM D790
Izod Impact, Notched 0.490 J/cm
0.918 ft-lb/in
DIN 53453; ASTM D256
Thermal Properties Metric English Comments
CTE, linear 70.0 µm/m-°C

@Temperature 20.0 °C
38.9 µin/in-°F

@Temperature 68.0 °F
DIN 53752; ASTM D696
Melting Point 255 °C
491 °F
DIN 53736; ASTM D789
Deflection Temperature at 0.46 MPa (66 psi) 230 °C
446 °F
DIN 53461; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
DIN 53461; ASTM D648
Flammability, UL94 HB
HB
Electrical Properties Metric English Comments
Dielectric Constant 3.4

@Frequency 1e+6 Hz
3.4

@Frequency 1e+6 Hz
ASTM D150/DIN 53483
Dielectric Strength 20.0 kV/mm
508 kV/in
ASTM D149/DIN 53481
Arc Resistance 128 sec
128 sec
ASTM D495