Kolon KOPA® KN333G15SIBL G/F Reinforced Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Glass Fiber Filled |
| Manufacturer | Kolon |
| Trade Name | Kopa® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kolon KOPA® KN333G15SIBL G/F Reinforced Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High strength, high toughnessApplications Relay coversInformation provided by API-Kolon.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.40 % | 0.40 % | 60% RH; ASTM D570 |
| Linear Mold Shrinkage | 0.0050 - 0.0080 cm/cm | 0.0050 - 0.0080 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength | 118 MPa | 17100 psi | ASTM D638 |
| Elongation at Break | 7.0 % | 7.0 % | ASTM D638 |
| Flexural Strength | 191 MPa | 27700 psi | ASTM D790 |
| Flexural Modulus | 5.492 GPa | 796.5 ksi | ASTM D790 |
| Izod Impact, Notched | 0.490 J/cm | 0.918 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 30.0 µm/m-°C | 16.7 µin/in-°F | ASTM D696 |
| Melting Point | 255 °C | 491 °F | ASTM D1525 |
| Deflection Temperature at 0.46 MPa (66 psi) | 245 °C | 473 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.4 | 3.4 | ASTM D150 |
| Dielectric Strength | 21.0 kV/mm | 533 kV/in | ASTM D149 |
| Arc Resistance | 135 sec | 135 sec | ASTM D495 |
Users viewing this material also viewed the following:
- RheTech Products G10P100-00 10% Glass Fiber Reinforced Polypropylene, Natural
- Honeywell Capran® Emblem™ 2500 Bi-Axially Oriented Nylon Film
- Teknor Apex Sinpolene MBB005LE Low Density Polyethylene
- A. Schulman POLYBATCH™ Red 5500 Concentrate Based In Polyethylene
- A. Schulman FORMION™ FI 401 Ionomer
- Crucible Steel 161 Tool Steel, High Carbon H13
- DuPont™ Nomex® 411 Paper, 10 mil Nominal Thickness
- ExxonMobil Vistalon™ 6602 Ethylene Propylene Diene Terpolymer Rubber
- Adamas Adalon® 902 PTFE, 1% Conductive filler
- Hexcel® Redux® 810 Two-Part Epoxy Paste Adhesive
Copyright © lookpolymers.com All Rights Reserved