- Kolon KOPA® KN333C22 CF Reinforced Nylon 66
Kolon KOPA® KN333C22 CF Reinforced Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Carbon Fiber Filled |
| Manufacturer | Kolon |
| Trade Name | Kopa® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kolon KOPA® KN333C22 CF Reinforced Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Carbon 22%, high strengthApplications Cylinder piston partsInformation provided by API-Kolon.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.23 g/cc | 1.23 g/cc | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.40 % | 0.40 % | 60% RH; ASTM D570 |
| Linear Mold Shrinkage | 0.0030 - 0.0070 cm/cm | 0.0030 - 0.0070 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 125 | 125 | ASTM D785 |
| Tensile Strength | 201 MPa | 29200 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Strength | 293 MPa | 42500 psi | ASTM D790 |
| Flexural Modulus | 9.905 GPa | 1437 ksi | ASTM D790 |
| Izod Impact, Notched | 0.980 J/cm | 1.84 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 20.0 µm/m-°C | 11.1 µin/in-°F | ASTM D696 |
| Melting Point | 255 °C | 491 °F | ASTM D1525 |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 247 °C | 477 °F | ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.6 | 3.6 | ASTM D150 |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | ASTM D149 |
| Arc Resistance | 140 sec | 140 sec | ASTM D495 |
Users viewing this material also viewed the following:
- Pyrotek AL-THERM 2100H Vacuum formed refractories for use with modular hot top systems
- SABIC Innovative Plastics Lexan® 920A PC
- Mitsubishi Xantar® SF 2230 Polycarbonate-30% Glass Reinforced
- Skamol Group SKAMOCAST 112-80 Insulating Castable
- Borealis Borclean™ HC300BF Polypropylene Homopolymer for Capacitor Film
- Zircar Refractory Composites RS-99M Refractory Sheet
- Dow Corning SILASTIC® 9220/55 KIT PARTS A&B
- DSM Novamid® 2620A PA6/6T
- ChevronTexaco Rykon® ISO 46 Premium Oil
- C.O.I.M. LARIPUR® LPR5850 Modified Ester Polyurethane
Copyright © lookpolymers.com All Rights Reserved