Kolon KOCETAL® K100 Standard Grade Acetal Resin
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced |
| Manufacturer | Kolon |
| Trade Name | Kocetal® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kolon KOCETAL® K100 Standard Grade Acetal Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Suitable for extrusion and injection molding of thick products. Applications: Extruded use such as rod, pipe, tube, and sheetInformation provided by API Kolon.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.41 g/cc | 1.41 g/cc | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.22 % | 0.22 % | 60% RH; ASTM D570 |
| Linear Mold Shrinkage | 0.022 cm/cm | 0.022 in/in | ASTM D955 |
| Melt Flow | 2.5 g/10 min | 2.5 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 78 | 78 | ASTM D785 |
| Tensile Strength | 57.0 MPa | 8270 psi | ASTM D638 |
| Elongation at Break | 80 % | 80 % | ASTM D638 |
| Flexural Strength | 80.0 MPa | 11600 psi | ASTM D790 |
| Flexural Modulus | 2.20 GPa | 319 ksi | ASTM D790 |
| Izod Impact, Notched | 0.870 J/cm | 1.63 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 130 µm/m-°C | 72.2 µin/in-°F | ASTM D696 |
| Melting Point | 166 °C | 331 °F | ASTM D1525 |
| Deflection Temperature at 0.46 MPa (66 psi) | 158 °C | 316 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | ASTM D648 |
| Vicat Softening Point | 162 °C | 324 °F | ASTM D1525 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | ASTM D257 |
| Dielectric Constant | 3.7 | 3.7 | ASTM D150 |
| Dielectric Strength | 19.0 kV/mm | 483 kV/in | ASTM D149 |
| Dissipation Factor | 0.0060 @Frequency 1.00e+6 Hz |
0.0060 @Frequency 1.00e+6 Hz |
ASTM D150 |
Users viewing this material also viewed the following:
- Northstar Polymers MPP-M09D "Slow Cure" Semi-Rigid Foam Formulation
- MarkeTech Silicon Single Crystal Semiconductor Wafer, n-type, Arsenic Doped, Czochralski-LED Grown
- Greene Tweed CHEMRAZ® 543 Perfluoroelastomer
- TIMCAL TIMREX® M100 mesh FR Natural Flake Graphite
- Trelleborg Offshore Vikotherm™ 73785 Insulative Elastomer
- A. Schulman SCHULADUR® A GB30 30% Glass Bead Reinforced PBT
- Denka VINYKON W4050 PVC, W grade for equipment cords, for heat resistance
- Akzo Nobel Trigonox® D-E50 Polymerization Initiator
- Trelleborg Horda Cable E7310 Bonded Insulation Shielding And Conductor Screen
Copyright © lookpolymers.com All Rights Reserved