Lavergne VYPET VNT 230 PET - PBT 30% Glass Reinforced Polyester
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , PBT + PET Blend, Glass Filled , Polyethylene Terephthalate (PET) |
| Manufacturer | Lavergne Performance Compounds |
| Trade Name | VYPET |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lavergne VYPET VNT 230 PET - PBT 30% Glass Reinforced Polyester.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Vypet VNT 230 is a 30% fiberglass reinforced modified PBT/PET polyester injection molding compound designed for electrical applications requiring improved surface aesthetics and improved UV resistance.Features: High temperature performance; Excellent strength and stiffness; Excellent dimensional stabilityTypical Applications: Electrical motors; ConnectorsInformation provided by Bieglo Gmbh for Lavergne Performance Compounds
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.51 g/cc | 0.0546 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm @Thickness 2.00 mm |
0.0040 in/in @Thickness 0.0787 in |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm @Thickness 2.00 mm |
0.010 in/in @Thickness 0.0787 in |
ASTM D955 |
| Ash | 30 % | 30 % | ASTM D2854 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 140 MPa | 20300 psi | 5 mm/min; ASTM D638 |
| Flexural Strength | 190 MPa | 27600 psi | 1.3 mm/min; ASTM D790 |
| Flexural Modulus | 9.80 GPa | 1420 ksi | 1.3 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.700 J/cm @Temperature 23.0 °C |
1.31 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 260 - 270 °C | 500 - 518 °F | |
| Middle Barrel Temperature | 270 - 275 °C | 518 - 527 °F | |
| Front Barrel Temperature | 275 - 280 °C | 527 - 536 °F | |
| Nozzle Temperature | 275 - 290 °C | 527 - 554 °F | |
| Melt Temperature | 275 - 290 °C | 527 - 554 °F | |
| Mold Temperature | 75.0 - 100 °C | 167 - 212 °F | |
| Injection Pressure | 55.0 - 85.0 MPa | 7980 - 12300 psi |
Users viewing this material also viewed the following:
- Huntsman Araldite GY 6008 Bisphenol A Epoxy Liquid Resin
- Mearthane Durethaneâ„¢ C Foams DCF and DCM Polyurethane
- H.C. Starck Amperit® 527.088 Agglomerated, Sintered Tungsten Carbide-Cobalt (WC-Co) 83-17
- Techmer ES HiFill® PA6 GF50 HS L 50% Glass Filled (Conditioned)
- Struktol POLYDIS 3680 Elastomer modified epoxy prepolymer
- A. Schulman POLYBATCH™ Navajo 10275U/4 Concentrate Based In LDPE
- Loctite® 3701 Acrylic Light Cure Adhesive
- Dow Corning MOLYKOTE® BG-20 SYNTHETIC BEARING GREASE
- Chosun Refractories CTL CGB-B Monolithic Refractories for Ladle and Tundish
- C.O.I.M. LARIPUR® LPR70D60 PTMG Polyether Polyurethane
Copyright © lookpolymers.com All Rights Reserved