Iran Petrochemical (PCC) LL0220KJ Linear Low Density Polyethylene
| Category | Polymer , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Butene, Film |
| Manufacturer | Iran Petrochemical Commercial Co. (PCC) |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Iran Petrochemical (PCC) LL0220KJ Linear Low Density Polyethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LL0220KJ are linear low density polyethylene copolymers containing butane-1 as the comonomer.Applications: shipping sacks, carrier and garbage bags, consumer packaging, high clarity film, agricultural film.Information provided by Iran Petrochemical Commercial Co.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in³ | ISO 1183 |
| Melt Flow | 2.3 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.3 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 10.0 MPa | 1450 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 11.0 MPa | 1600 psi | ASTM D882 |
| Film Elongation at Break, MD | 1000 % | 1000 % | ASTM D882 |
| Film Elongation at Break, TD | 1100 % | 1100 % | ASTM D882 |
| 2% Secant Modulus | 0.0800 GPa | 11.6 ksi | MD; ASTM D882 |
| 0.100 GPa | 14.5 ksi | TD; ASTM D882 | |
| Coefficient of Friction | 0.13 | 0.13 | ASTM D1894 |
| Elmendorf Tear Strength MD | 100 g | 100 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 300 g | 300 g | ASTM D1922 |
| Dart Drop Test | 90.0 g | 0.198 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 30.0 MPa | 4350 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 25.0 MPa | 3630 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 100 °C | 212 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 12 % | 12 % | ASTM D1003 |
| Gloss | 30 % | 30 % | ASTM D2457 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 123 °C | 253 °F | |
| 225 °C | 437 °F |
Users viewing this material also viewed the following:
- Lubrizol Advanced Materials PEARLTHANE® 16N92 Thermoplastic Polyurethane Elastomer (discontinued **)
- Hardwire 3SX-21.5-12 High Density Composite
- Silberline Tufflake® 4700
- Solvay MACKAM® 35 UL Surfactant
- ExxonMobil PP2252E3 Homopolymer
- Diamond Polymers NPP11-0119 Linear Low Density Polyethylene with Antiblock
- C.O.I.M. EXTER S® S 203 Special Laminate
- 3M FP101 Clear Polypropylene Label Product
- LG Chemical i-BuOH Isobutyl Alcohol
Copyright © lookpolymers.com All Rights Reserved