Inno-Comp INNOPOL® CS 2-2130 30% Talc Filled Polypropylene Copolymer
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Talc Filler |
| Manufacturer | Inno-Comp Ltd |
| Trade Name | INNOPOL® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Inno-Comp INNOPOL® CS 2-2130 30% Talc Filled Polypropylene Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
INNOPOL® CS 2-2130 is a 30 % talc-filled polypropylene compound /PP-B TD30 (ISO 1043)/. This grade is available in natural and custom colored form.INNOPOL® CS 2-2130 is recommended for producing injection molded automotive products where the required property is high stiffness besides low shrinkage and low temperature resistance.Information provided by INNO-COMP
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ISO 1183 |
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 230 °C |
20 g/10 min @Load 4.76 lb, Temperature 446 °F |
nozzle diam 2.095 mm; ISO 1133 |
| Storage Temperature | <= 60.0 °C | <= 140 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 28.0 MPa | 4060 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Yield | 3.0 % | 3.0 % | 50 mm/min; ISO 527-1,-2 |
| Tensile Modulus | 3.10 GPa | 450 ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Modulus | 3.20 GPa | 464 ksi | ISO 178 |
| Charpy Impact, Notched | 0.200 J/cm² @Temperature -20.0 °C |
0.952 ft-lb/in² @Temperature -4.00 °F |
ISO 179/1eA |
| 0.350 J/cm² @Temperature 23.0 °C |
1.67 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 126 °C | 259 °F | ISO 75-1,-2 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 210 - 240 °C | 410 - 464 °F | Injection |
| Middle Barrel Temperature | 210 - 240 °C | 410 - 464 °F | Injection |
| Front Barrel Temperature | 210 - 240 °C | 410 - 464 °F | Injection |
| Melt Temperature | 230 - 250 °C | 446 - 482 °F | Injection |
| Mold Temperature | 15.0 - 50.0 °C | 59.0 - 122 °F | |
| Moisture Content | <= 0.070 % | <= 0.070 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Resin Designation | PP-B TD30 | ISO 1043 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Geloy FXTW30PE ASA
- PolyOne Dynaflex™ G2780-0001 Thermoplastic Elastomer (TPE)
- Reliance Industries Repol H200MA Polypropylene
- Freudenberg Simrit N470 Nitrile Elastomer (NBR)
- SABIC Innovative Plastics LNP STAT-KON Noryl_HMC1010 PPE+HIPS (Europe-Africa-Middle East)
- Shinkong Synthetic Fibers Shinite® D202G15 PBT, 15% Glass Filled, Fire Retardant
- Cossa Polimeri ESTACARB 0820 GF V0-5V HF Flame Retardant Polycarbonate
- Colorite Polymers CS7559LS Wire and Cable Insulation Vinyl Compound
- DuPont Performance Polymers Crastin® LW9030 BK851 PBT (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved