Braskem Green PE SLH0820/30AF Blow Film Extrusion and Cast Film Extrusion Linear Low Density Polyethylene

Category Polymer , Film , Renewable/Recycled Polymer , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade
Manufacturer Braskem
Trade Name Green PE
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Braskem Green PE SLH0820/30AF Blow Film Extrusion and Cast Film Extrusion Linear Low Density Polyethylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: SLH0820/30AF is a LLDPE hexene copolymer produced by Braskem. It offers outstanding processability combined with excellent mechanical properties. Very low gel amount. The minimum biobased content of this grade is 84%, determined according to ASTM D6866. Additive: Slip Absent; Processing Aid Medium; Antiblocking High Applications: Lamination; Heavy duty bags; Blends with LDPE and HDPE; Valvulated heavy duty bagsInformation provided by Braskem.
Physical Properties Metric English Comments
Specific Gravity 0.920 g/cc
0.920 g/cc
ASTM D1505/D792
Thickness 25.0 microns
0.984 mil
Melt Flow 0.80 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.80 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 950 %
950 %
ASTM D882
Film Elongation at Break, TD 1180 %
1180 %
ASTM D882
Elmendorf Tear Strength MD 270 g
270 g
gF; ASTM D1922
Elmendorf Tear Strength TD 500 g
500 g
gF; ASTM D1922
Dart Drop Test 170 g
0.375 lb
g/F50; ASTM D1709
Film Tensile Strength at Break, MD 50.0 MPa
7250 psi
ASTM D882
Film Tensile Strength at Break, TD 40.0 MPa
5800 psi
ASTM D882
1% Secant Modulus, MD 170 MPa
24700 psi
ASTM D882
1% Secant Modulus, TD 180 MPa
26100 psi
ASTM D882