- HOME
- POLYMER SEARCH
- Thermoplastic
- Polypropylene (PP)
- Polypropylene with 40% Talc Filler
- Inno-Comp INNOPOL® CS 1-5140 BLH 40% Talc-Filled Polypropylene Homopolymer
Inno-Comp INNOPOL® CS 1-5140 BLH 40% Talc-Filled Polypropylene Homopolymer
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 40% Talc Filler |
| Manufacturer | Inno-Comp Ltd |
| Trade Name | INNOPOL® CS |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Inno-Comp INNOPOL® CS 1-5140 BLH 40% Talc-Filled Polypropylene Homopolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
INNOPOL® CS 1-5140 BLH is a 40% talc-filled polypropylene homopolymer compound /PP-H TD40 (ISO 1043)/.INNOPOL® CS 1-5140 BLH is recommended especially for producing products, where high stiffness, low shrinkage and long term heat stability are required.All information provided by INNO-COMP.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc @Temperature 23.0 °C |
0.0441 lb/in³ @Temperature 73.4 °F |
ISO 1183 |
| Melt Flow | 14.5 g/10 min @Load 5.00 kg, Temperature 230 °C |
14.5 g/10 min @Load 11.0 lb, Temperature 446 °F |
ISO 1133 |
| Ash | 37 % @Temperature 600 °C |
37 % @Temperature 1110 °F |
ISO 3451-1/A |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 31.0 MPa | 4500 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Break | 7.0 % | 7.0 % | ISO 527-1,-2 |
| Elongation at Yield | 3.6 % | 3.6 % | 50 mm/min; ISO 527-1,-2 |
| Tensile Modulus | 4.00 GPa | 580 ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Modulus | 4.10 GPa | 595 ksi | 2 mm/min; ISO 178 |
| Charpy Impact Unnotched | 1.30 J/cm² @Temperature -30.0 °C |
6.19 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 3.00 J/cm² @Temperature 23.0 °C |
14.3 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.160 J/cm² @Temperature -30.0 °C |
0.761 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 0.350 J/cm² @Temperature 23.0 °C |
1.67 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 133 °C | 271 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 79.0 °C | 174 °F | ISO 75-1,-2 |
| Vicat Softening Point | 93.0 °C | 199 °F | B120; ISO 306 |
| 156 °C | 313 °F | A120; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
FMVSS 302 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Black |
Users viewing this material also viewed the following:
- Polymax® Maxelast® P3975H TPE, PP Overmold or Standalone use
- PSM Industries Pacific Sintered Metals Silicon Iron FS-1603 Powdered Metal
- Premix Premi-Glas® 2103-10 CRSX Polyester BMC
- Karina 600D48/1-A-IS-BZ Black PVC Compound
- Monmouth Rubber & Plastics Durafoamâ„¢ C42NBR Nitrile Rubber
- Borealis Daplen™ EF267AI Polypropylene TPO Compound
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 40 PHR Non-Black, Soft Clay
- Cossa Polimeri ESTAPROP 1040 V2 H Flame Retardant Polypropylene
- Dow DOWLEX™ 2070G Linear Low Density Polyethylene
- Arkema Group LOTRYL® 37 EH 550 Copolymer Ethylene - Acrylic Ester
Copyright © lookpolymers.com All Rights Reserved