- Special Metals INCONEL® 706 Precipitation Hardening Alloy, Cold Rolled Sheet, 2 Part Heat Treatment, 0.040 inch (1.02 mm) Thickness
Special Metals INCONEL® 706 Precipitation Hardening Alloy, Cold Rolled Sheet, 2 Part Heat Treatment, 0.040 inch (1.02 mm) Thickness
| Category | Metal , Nonferrous Metal , Nickel Alloy , Superalloy |
| Manufacturer | Special Metals (includes the former Inco Alloys International Inc.) |
| Trade Name | INCONEL® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Special Metals INCONEL® 706 Precipitation Hardening Alloy, Cold Rolled Sheet, 2 Part Heat Treatment, 0.040 inch (1.02 mm) Thickness.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Tensile strength (ultimate and yield), shear strength, and elongation values reported here are typical for Cold Rolled Sheet, 2 Part Heat Treatment, 0.040 inch (1.02 mm) Thickness samples. Density and magnetic permeability are typical of precipitation hardened INCONEL® alloy 706. Other property values are typical of INCONEL® alloy 706.For tensile-limited applications, the alloy receives a two part heat treatment as follows: Solution treat 1700-1850°F (925-1010°C) for a time commensurate with section size, then air cool. Precipitation treatment 1350°F (730°C)/8 hr, furnace cool at 100°F (55°C)/hr to 1150°F (620°C)/8 hr, air cool.Data provided by the manufacturer, Special Metals.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 8.08 g/cc | 0.292 lb/in³ | Precipitation Hardened |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 1334 MPa | 193500 psi | |
| Tensile Strength, Yield | 1112 MPa @Strain 0.200 % |
161300 psi @Strain 0.200 % |
|
| Elongation at Break | 24 % | 24 % | |
| Modulus of Elasticity | 210 GPa | 30500 ksi | Dynamic Method |
| Poissons Ratio | 0.382 | 0.382 | Calculated by mfr. |
| Shear Modulus | 76.0 GPa | 11000 ksi | Dynamic Method |
| Shear Strength | 825.3 MPa | 119700 psi | Thickness not reported for this value |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 13.46 µm/m-°C @Temperature 24.0 - 100 °C |
7.478 µin/in-°F @Temperature 75.2 - 212 °F |
Mean |
| 15.08 µm/m-°C @Temperature 24.0 - 300 °C |
8.378 µin/in-°F @Temperature 75.2 - 572 °F |
Mean | |
| 15.59 µm/m-°C @Temperature 24.0 - 500 °C |
8.661 µin/in-°F @Temperature 75.2 - 932 °F |
Mean | |
| 16.42 µm/m-°C @Temperature 21.0 - 700 °C |
9.122 µin/in-°F @Temperature 69.8 - 1290 °F |
Mean | |
| Specific Heat Capacity | 0.444 J/g-°C | 0.106 BTU/lb-°F | |
| Thermal Conductivity | 12.5 W/m-K | 86.8 BTU-in/hr-ft²-°F | |
| Melting Point | 1334 - 1371 °C | 2433 - 2500 °F | |
| Solidus | 1334 °C | 2433 °F | |
| Liquidus | 1371 °C | 2500 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Aluminum, Al | <= 0.060 % | <= 0.060 % | |
| Boron, B | <= 0.0060 % | <= 0.0060 % | |
| Carbon, C | <= 0.30 % | <= 0.30 % | |
| Chromium, Cr | 14.5 - 17.5 % | 14.5 - 17.5 % | |
| Cobalt, Co | <= 1.0 % | <= 1.0 % | |
| Copper, Cu | <= 0.35 % | <= 0.35 % | |
| Iron, Fe | 38 % | 38 % | As remainder |
| Manganese, Mn | <= 0.35 % | <= 0.35 % | |
| Nickel, Ni | 39 - 44 % | 39 - 44 % | Including Cobalt |
| Niobium, Nb (Columbium, Cb) | 2.5 - 3.3 % | 2.5 - 3.3 % | Includes Ta |
| Phosphorous, P | <= 0.020 % | <= 0.020 % | |
| Silicon, Si | <= 0.35 % | <= 0.35 % | |
| Sulfur, S | <= 0.015 % | <= 0.015 % | |
| Titanium, Ti | <= 0.40 % | <= 0.40 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.0000985 ohm-cm | 0.0000985 ohm-cm | |
| Magnetic Permeability | 1.01 | 1.01 | at 200 Oersted (15.9 kA/m);Annealed |
| Curie Temperature | <= -78.0 °C | <= -108 °F |
Users viewing this material also viewed the following:
- Nanocyl NANOCYL™ NC1100 Single-Wall Isolated and Bundled Carbon Nanotubes - Research grade
- Nilit Polynil® P50 Standard Viscosity Nylon 66
- Chevron Phillips Marlex® 9506H High Performance Series HDPE Blow Molding Resin (discontinued **)
- Hexion Bakelite™ PF 85 Phenolic Formaldehyde Resin, UL Listed (discontinued **)
- SABIC Innovative Plastics LNP STAT-KON DEF42 PC (Asia Pacific)
- SABIC Innovative Plastics LNP Stat-kon WEF42 PET/PBT
- Dow Corning SILASTIC® V RTV SILICONE RUBBER BASE & CURING AGENT
- Chevron Phillips 6109L LLDPE Blown Film Resin, Butene Copolymer (discontinued **)
Copyright © lookpolymers.com All Rights Reserved