Ineos Styrenics Polystyrene 168M0 (NAFTA)
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Heat Resistant Grade |
| Manufacturer | Ineos Styrenics |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos Styrenics Polystyrene 168M0 (NAFTA).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High heat, high molecular weight general purpose polystyrene with low residual volatiles. It is ideally suited for use in critical low taste, low odor food packaging products.Information provided by BASF.Ineos Styrenics purchased this product line from BASF in 2005.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | |
| Linear Mold Shrinkage | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 1.5 g/10 min @Load 5.00 kg, Temperature 200 °C |
1.5 g/10 min @Load 11.0 lb, Temperature 392 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 78 | 78 | ASTM D785 |
| Tensile Strength, Ultimate | 52.0 MPa | 7540 psi | |
| Elongation at Break | 3.0 % | 3.0 % | |
| Tensile Modulus | 2.55 GPa | 370 ksi | |
| Flexural Modulus | 3.31 GPa | 480 ksi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | |
| Vicat Softening Point | 109 °C | 228 °F | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 210 - 240 °C | 410 - 464 °F | Extrusion |
Users viewing this material also viewed the following:
- Nabaltec APYMAG® 60 Magnesium Hydroxide
- Potters Industries Conduct-O-Fil® SH400S20 Silver-Coated Hollow Glass Spheres
- Solvay Specialty Polymers Solef® 21508 PVDF Copolymer (discontinued **)
- MetalTek NAVY G Cast UNS C90300 Bearing Bronze
- SYNTHOS Forsan® 483 Acrylonitrile Butadiene Styrene (ABS)
- Samsung Cheil Industries Starex® GR-4017 ABS, Glass Filled
- Cheng Yu Plastic T882GV1 Flame Retardant PBT, 10% Glass Fiber
- ChevronTexaco Supreme SAE 40 Motor Oil
- BASF Neopolen® P 9435 0.05 g/cc Core density; Expanded Polypropylene (Europe)
- Sinotek Materials W80-Z Amorphous Graphite Grain
Copyright © lookpolymers.com All Rights Reserved