Ineos Styrenics Avantra® 594E High Impact Styrenic Polymer (NAFTA)
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified |
| Manufacturer | Ineos Styrenics |
| Trade Name | Avantra® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos Styrenics Avantra® 594E High Impact Styrenic Polymer (NAFTA).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Avantra® 594E is a super high-impact polystyrene grade that delivers excellent processing efficiency along with toughness and high gloss in a wide variety of injection molding applications such as consumer electronics, office equipment, building & construction, housewares, office products, cosmetics & personal care products, recreation equipment & sporting goods, toys, and furniture & furnishings.Information provided by BASF.Ineos Styrenics purchased this product line from BASF in 2005.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ASTM D792 |
| Moisture Absorption at Equilibrium | <= 0.10 % | <= 0.10 % | 23°C/50% RH |
| Water Absorption at Saturation | <= 0.10 % | <= 0.10 % | |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 8.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
8.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell L | 55 | 55 | ASTM D785 |
| Tensile Strength at Break | 17.0 MPa | 2470 psi | ASTM D638 |
| Tensile Strength, Yield | 20.0 MPa | 2900 psi | ASTM D638 |
| Elongation at Break | 60 % | 60 % | ASTM D638 |
| Tensile Modulus | 2.068 GPa | 299.9 ksi | ASTM D638 |
| Flexural Modulus | 2.275 GPa | 330.0 ksi | ASTM D790-1 |
| Izod Impact, Notched | 1.82 J/cm | 3.40 ft-lb/in | ASTM D256-A |
| Gardner Impact | 36.2 J @Thickness 3.17 mm, Temperature 23.0 °C |
26.7 ft-lb @Thickness 0.125 in, Temperature 73.4 °F |
ASTM D5420, GB |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 79.0 °C | 174 °F | ASTM D648 |
| Vicat Softening Point | 97.0 °C | 207 °F | ASTM D1525 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
all colors |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 70 % | 70 % | 60°; ASTM D523 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 180 - 280 °C | 356 - 536 °F | Molding |
Users viewing this material also viewed the following:
- Qualchem Danamid FELX0 Polyamide 6
- PolyOne Geon™ Vinyl Flexible C6500 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Lubrizol Pellethane® 2363-90A Thermoplastic Polyurethane Elastomer
- ExxonMobil Exceed™ 4518PA Premium Cast Film Resin
- DuPont Teijin Films Teijin® Tetoron® U2 Polyester Film, 200 Gauge
- Arlon 28540R015 0.016" (0.406 mm) Uncured Silicone Rubber with Fiberglass Substrate
- ConocoPhillips Hydroclear® 46 AW Hydraulic Fluid
- Ascend Performance Materials Vydyne® R860 BK02 Nylon 66, Glass/Mineral Reinforced, Conditioned
- SABIC Innovative Plastics LNP STAT-KON Noryl_FMC1010 PPE+PS
- Ametek P303L P/M Stainless Steel, Sintered from 6.5 g/cc Green Density
Copyright © lookpolymers.com All Rights Reserved