Ineos ABS Triax® 3050 ABS/Nylon Alloy, Injection Molding Grade (DAM)
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS)/Nylon Blend , Nylon |
| Manufacturer | Ineos ABS |
| Trade Name | Triax® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos ABS Triax® 3050 ABS/Nylon Alloy, Injection Molding Grade (DAM).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Triax® 3050 resin is an ABS (Acrylonitrile Butadiene Styrene)/Nylon 6 alloy for injection molding. It is a semicrystalline thermoplastic with improved stability to light exposure, excellent processability, good chemical resistance, good fatigue performance, and excellent abrasion characteristics. Triax® 3050 resin exhibits a good balance of impact strength and flow properties. Typical applications include interior automotive applications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.06 g/cc | 1.06 g/cc | ASTM-D792 |
| Density | 1.05 g/cc | 0.0380 lb/in³ | ASTM-D792 |
| Water Absorption | 1.1 % @Time 86400 sec |
1.1 % @Time 24.0 hour |
ASTM-D570 |
| Water Absorption at Saturation | 4.3 % | 4.3 % | ASTM-D570 |
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | ASTM-D955 |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | ASTM-D955 |
| Melt Flow | 6.0 g/10 min @Load 5.00 kg, Temperature 260 °C |
6.0 g/10 min @Load 11.0 lb, Temperature 500 °F |
ASTM-D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 105 | 105 | ASTM-D785 |
| Tensile Strength, Yield | 43.4 MPa | 6300 psi | ASTM-D638 |
| Elongation at Break | >= 50 % | >= 50 % | ASTM-D638 |
| Tensile Modulus | 2.17 GPa | 315 ksi | ASTM-D638 |
| Flexural Yield Strength | 75.2 MPa | 10900 psi | ASTM-D790 |
| Flexural Modulus | 2.07 GPa | 300 ksi | ASTM-D790 |
| Izod Impact, Notched | 0.694 J/cm @Thickness 6.35 mm, Temperature -40.0 °C |
1.30 ft-lb/in @Thickness 0.250 in, Temperature -40.0 °F |
ASTM-D256 |
| 0.801 J/cm @Thickness 3.17 mm, Temperature -40.0 °C |
1.50 ft-lb/in @Thickness 0.125 in, Temperature -40.0 °F |
ASTM-D256 | |
| 7.47 J/cm @Thickness 6.35 mm, Temperature 22.8 °C |
14.0 ft-lb/in @Thickness 0.250 in, Temperature 73.0 °F |
ASTM-D256 | |
| 8.01 J/cm @Thickness 3.17 mm, Temperature 22.8 °C |
15.0 ft-lb/in @Thickness 0.125 in, Temperature 73.0 °F |
ASTM-D256 | |
| Impact Test | 47.5 J @Temperature -40.0 °C |
35.0 ft-lb @Temperature -40.0 °F |
Instrumented Impact, Total Energy: 0.100-in.; 0.5-in. dart; 1.6-in. clamp; 7.6 mph; ASTM-D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 90.0 °C @Thickness 3.17 mm |
194 °F @Thickness 0.125 in |
Unannealed; ASTM-D648 |
| 97.2 °C @Thickness 6.35 mm |
207 °F @Thickness 0.250 in |
Unannealed; ASTM-D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C @Thickness 3.17 mm |
149 °F @Thickness 0.125 in |
Unannealed; ASTM-D648 |
| 73.9 °C @Thickness 6.35 mm |
165 °F @Thickness 0.250 in |
Unannealed; ASTM-D648 | |
| Vicat Softening Point | 185 °C @Load 1.00 kg |
365 °F @Load 2.20 lb |
Rate B, 120°C/hour; ASTM-D1525 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 8.30e+15 ohm | 8.30e+15 ohm | ASTM-D257 |
| Dielectric Constant | 3.5 @Frequency 1.00e+6 Hz |
3.5 @Frequency 1.00e+6 Hz |
Tinfoil Electrodes; ASTM-D150 |
| Dielectric Strength | 16.7 kV/mm @Thickness 1.57 mm |
425 kV/in @Thickness 0.0620 in |
Short time under oil; ASTM-D149 |
| Dissipation Factor | 0.024 @Frequency 1.00e+6 Hz |
0.024 @Frequency 1.00e+6 Hz |
Tinfoil Electrodes; ASTM-D150 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 232 - 266 °C | 450 - 511 °F | Injection Molding |
| Middle Barrel Temperature | 232 - 266 °C | 450 - 511 °F | Injection Molding |
| Front Barrel Temperature | 232 - 266 °C | 450 - 511 °F | Injection Molding |
| Nozzle Temperature | 249 - 260 °C | 480 - 500 °F | Injection Molding |
| Melt Temperature | 238 - 271 °C | 460 - 520 °F | Injection Molding |
| Mold Temperature | 38.0 - 66.0 °C | 100 - 151 °F | Injection Molding |
| Drying Temperature | 88.0 °C @Time 7200 - 14400 sec |
190 °F @Time 2.00 - 4.00 hour |
|
| Moisture Content | 0.15 - 0.35 % | 0.15 - 0.35 % | |
| Dew Point | <= -29.0 °C | <= -20.2 °F | inlet air |
| Injection Pressure | 41.4 - 82.7 MPa | 6000 - 12000 psi | Injection Molding |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi | Injection Molding |
| Clamp Pressure | 46.2 - 77.0 MPa | 6700 - 11200 psi | Injection Molding |
| Cushion | <= 0.317 cm | <= 0.125 in | Injection Molding |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Hold Pressure | 30-50% of Injection Pressure, Injection Molding | |
| Injection Speed | Fast | Injection Molding |
| Screw Compression Ratio | 2.5:1 | Injection Molding |
| Screw Length-to-Diameter Ratio | >= 20:1 | Injection Molding |
| Screw Speed | Moderate, Injection Molding | |
| Shot Weight-to-Machine Capacity Ratio | 0.5-0.7 | Injection Molding |
Users viewing this material also viewed the following:
- LyondellBasell Petrothene® NA345013 Low Density Polyethylene (Film Extrusion)
- IRPC Polimaxx Porene AP102 Acrylonitrile Butadiene Styrene
- Sumitomo Chemical ESPOLEX® 817 Thermoplastic Elastomer
- Hexcel® HexWeb® CR-PAA™ 1/8-5052-0.0037 Phosphoric Acid Anodized Aluminum Honeycomb
- Dow Corning HS II BASE & 10:1 CLAY CATALYST
- Chicago Extruded Metals BioBrass® UNS C62300 Aluminum Bronze
- DuPont Performance Polymers Rynite® 935 BK505 Polyethylene Terephthalate (PET) (Unverified Data**)
- CMT Materials HYTAC® FLXT High Temperature, PTFE Impregnated Copolymer Syntactic
- Axiall EX1063 Coax & Telecom Flexible PVC
- PolyOne Elastamax™ XL 0141-115 Styrene Butadiene Block Copolymer (SBC) (discontinued **)
Copyright © lookpolymers.com All Rights Reserved