ExxonMobil LDPE LD 157CW Blown Low Density Polyethylene Resin

Category Polymer , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer Exxon Chemical
Trade Name LDPE
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil LDPE LD 157CW Blown Low Density Polyethylene Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: LD 157CW offer good mechanical properties as well as excellent opticals.Availability: Africa & Middle East and Europe Additive: Antiblock: NoSlip: NoThermal Stabilizer: YesApplications: Co-Extrusion FilmsLabel FilmLamination FilmMedium Duty Shrink FilmOverwrap FilmInformation provided by ExxonMobil
Physical Properties Metric English Comments
Density 0.931 g/cc
0.0336 lb/in³
ExxonMobil method
Melt Flow 0.60 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.60 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, TD 15.9 MPa
2300 psi
ASTM D882
Film Elongation at Break, MD 450 %
450 %
ASTM D882
Film Elongation at Break, TD 600 %
600 %
ASTM D882
Elmendorf Tear Strength MD 200 g
200 g
ASTM D1922
Elmendorf Tear Strength TD 230 g
230 g
ASTM D1922
Dart Drop Test 110 g
0.243 lb
ASTM D1709A
Film Tensile Strength at Break, MD 28.3 MPa
4100 psi
ASTM D882
Film Tensile Strength at Break, TD 24.1 MPa
3500 psi
ASTM D882
1% Secant Modulus, MD 352 MPa
51000 psi
ASTM D882
1% Secant Modulus, TD 379 MPa
55000 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point <= 239 °C
<= 462 °F
Peak Melting Point; ExxonMobil method
Optical Properties Metric English Comments
Haze 7.0 %
7.0 %
ASTM D1003
Gloss 65 %
65 %
45°; ASTM D2457