Ineos ABS Centrex® HGM ASA Blend (discontinued **)

Category	Polymer , Thermoplastic , ASA Polymer , Acrylonitrile/Styrene/Acrylate (ASA), Unreinforced, Molded
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Ineos ABS Centrex® HGM ASA Blend (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Key Features:UnfilledLight stabilized or stable to lightU.V. stabilized or stable to weatherHeat stabilized or stable to heatSuitable processing methods:Injection moldingInformation provided by Bayer Polymers.LANXESS was spun-off from Bayer in early 2005. Business renamed Ineos ABS after INEOS acquires a majority shareholding under a JV with Lanxess in 2007. Subsequently Ineos acquired 100% of Ineos ABS.

Physical Properties	Metric	English	Comments
Density	1.07 g/cc	0.0387 lb/in³
Melt Flow	4.9 g/10 min @Load 10.0 kg, Temperature 220 °C	4.9 g/10 min @Load 22.0 lb, Temperature 428 °F	cm³/10 min.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	41.0 MPa	5950 psi
Elongation at Break	25 %	25 %	Nominal
Elongation at Yield	3.0 %	3.0 %
Tensile Modulus	2.14 GPa	310 ksi
Charpy Impact, Notched	2.13 J/cm²	10.1 ft-lb/in²
	0.110 J/cm² @Temperature -30.0 °C	0.524 ft-lb/in² @Temperature -22.0 °F

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	121 µm/m-°C @Temperature 20.0 °C	67.2 µin/in-°F @Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi)	94.0 °C	201 °F
Deflection Temperature at 1.8 MPa (264 psi)	80.0 °C	176 °F
Vicat Softening Point	101 °C	214 °F	50°C/h 50N

Processing Properties	Metric	English	Comments
Melt Temperature	250 °C	482 °F	Injection Molding
Mold Temperature	60.0 °C	140 °F	Injection Molding
Injection Velocity	200 mm/sec	7.87 in/sec
Injection Pressure	60.0 MPa	8700 psi