A. Schulman POLYFORT™ FPP 1603 Glass Reinforced Copolymer
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 10% Glass Fiber Filler |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman POLYFORT™ FPP 1603 Glass Reinforced Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
DescriptionPolyfort® FPP 1603 is a 10% glass reinforced copolymer. It has good impact and heat resistance. Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.970 g/cc | 0.970 g/cc | ASTM D792 |
| Melt Flow | 8.0 g/10 min | 8.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 80 | 80 | ASTM D785 |
| Tensile Strength, Yield | 21.0 MPa | 3050 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Modulus | 1.90 GPa | 276 ksi | ASTM D790 |
| Izod Impact, Notched | 1.60 J/cm | 3.00 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 116 °C | 241 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 77.0 °C | 171 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Polymax® Maxelast® C4970 TPE, Transparent
- Chevron Phillips HiD® 9062 HDPE Injection Molding Resin (discontinued **)
- Solvay TECHNYL® B 230 PA66/6, Conditioned
- Hexcel® HexForce™ XLS9114 Carbon/Wire Fabric
- Chengdu Polyster FH3303 Thermoplastic Polyether-ester Elastomer (TPEE)
- Dow AFFINITY™ FM 1570 Polyolefin Plastomer
- CMW® ELKONITE® 3W53 Heat Treatable Tungsten Copper material
- BASF Elastollan® 695A15N Polyester Type Polyurethane Elastomer
Copyright © lookpolymers.com All Rights Reserved