Gromax CFG45-RN13N1 Nylon 6 46% Glass Filled (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 50% Glass Fiber Filled |
| Manufacturer | Gromax |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Gromax CFG45-RN13N1 Nylon 6 46% Glass Filled (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Gromax Enterprises Corp.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.60 g/cc | 1.60 g/cc | ISO 1183 |
| Moisture Absorption | 0.760 % | 0.760 % | ISO 62 |
| Maximum Moisture Content | 0.10 | 0.10 | Karl Fischer |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Temperature 80.0 °C |
0.0020 in/in @Temperature 176 °F |
60x60x2 mm; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm @Temperature 80.0 °C |
0.0060 in/in @Temperature 176 °F |
60x60x2 mm; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 90 | 90 | [N/mm<sup>2<sup>]; ISO 7619 |
| Tensile Strength | 196 MPa | 28400 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | 50 mm/min; ISO 527 |
| Flexural Strength | 290 MPa | 42100 psi | 5 mm/min; ISO 178 |
| Flexural Modulus | 11.4 GPa | 1650 ksi | 5 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 17.7 kJ/m² | 8.42 ft-lb/in² | ISO 180-1A |
| Charpy Impact Unnotched | 9.60 J/cm² @Temperature 23.0 °C |
45.7 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eU |
| Charpy Impact, Notched | 1.88 J/cm² @Temperature 23.0 °C |
8.95 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C | 460 °F | ISO 75-1,-2 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 266 - 280 °C | 511 - 536 °F | ISO 294 |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | ISO 294 |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2.00 - 6.00 hour | 2.00 - 6.00 hour |
Users viewing this material also viewed the following:
- Polymax® Maxelast® P1765B TPE, PP Overmold or Standalone use
- Kazanorgsintez Pyrolysis Heavy Resin
- Indium Corp. Indalloy® 238 Sn-Au Solder Alloy
- Lushan L-5R (F) Polyethylene Copolymer Adhesive for Steel Pipe Coating
- SABIC Innovative Plastics LNP THERMOCOMP EC005 PEI
- E-Polymers Tekaster® F615GFR , Flame Retardant, 30% Glass Reinforced PET
- California Fine Wire Alloy 417 Precious Metal Alloy
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber, 0.35 PHR Caytur 4
- Beijing Evergrow Resources ER-WR-30G Polypropylene Super-Fine Filter Material
- Schmolz + Bickenbach Cryodur® 2510 (O-1) Cold Work Die Steel
Copyright © lookpolymers.com All Rights Reserved