- SABIC Innovative Plastics LNP Lubricomp DP003XXP PC (Europe-Africa-Middle East)
SABIC Innovative Plastics LNP Lubricomp DP003XXP PC (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Lubricomp DP003XXP PC (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* DP003XXP is a compound based on Polycarbonate resin containing PTFE, Silicone. Added features include: Internally Lubricated.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.26 g/cc | 0.0455 lb/in³ | ISO 1183 |
| Water Absorption | 0.29 % @Temperature 23.0 °C, Time 86400 sec |
0.29 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm | 0.0060 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 51.0 MPa | 7400 psi | 50 mm/min; ISO 527 |
| Elongation at Yield | 5.6 % | 5.6 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 2.00 GPa | 290 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 80.0 MPa | 11600 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.20 GPa | 319 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 20.0 kJ/m² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 110 kJ/m² @Temperature 23.0 °C |
52.3 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Coefficient of Friction, Dynamic | 0.10 | 0.10 | ASTM D 3702 Modified |
| Coefficient of Friction, Static | 0.26 | 0.26 | ASTM D 3702 Modified |
| K (wear) Factor | 84.6 x 10-8 mm³/N-M | 42.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D 3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 75.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
41.7 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 78.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
43.3 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 126 °C | 259 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Flammability, UL94 | V-1 @Thickness 3.00 mm |
V-1 @Thickness 0.118 in |
UL 94 |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Flexible G92D Polyvinyl Chloride, Flexible (PVC, Flexible)
- PolyOne Geon™ Vinyl Flexible R363MB White 1876 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Honeywell Capran® Emblem™ 1200M Bi-Axially Oriented Nylon 6 Film
- Menzolit Menzolit® SMC 1100 Unsaturated Polyester UP
- Teknor Apex APEX® 90-A471R-80-NT Polyvinyl Chloride, Flexible
- PlastxWorld CEVIAN® B5536 30% GF PBT/ABS Alloy
- Clariant Renol PA143G10 Nylon 6/66 Copolymer, 10% Glass Fiber, Heat Stabilized
- Fainplast Compounds GSK 88 Flexible PVC, Injection Molding, Lead Free
- Braskem LF118 LLDPE Blown Film Extrusion Polyethylene Copolymer
- Loctite® PRISM® 4204 Instant Adhesive
Copyright © lookpolymers.com All Rights Reserved