Indium Corp. Indalloy 257 Bismuth Solder Alloy
| Category | Metal , Nonferrous Metal , Bismuth Alloy , Solder/Braze Alloy |
| Manufacturer | Indium Corporation of America |
| Trade Name | Indalloy |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Indium Corp. Indalloy 257 Bismuth Solder Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information Provided by Indium Corporation
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 9.69 g/cc | 0.350 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 34.9 MPa | 5060 psi | |
| Elongation at Break | 148.6 % | 148.6 % | |
| Modulus of Elasticity | 14.3 GPa | 2080 ksi | |
| Shear Strength | 26.2 MPa | 3800 psi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 24.0 µm/m-°C @Temperature 20.0 °C |
13.3 µin/in-°F @Temperature 68.0 °F |
|
| Melting Point | 95.0 - 96.0 °C | 203 - 205 °F | |
| Solidus | 95.0 °C | 203 °F | |
| Liquidus | 96.0 °C | 205 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Bismuth, Bi | 52 % | 52 % | |
| Lead, Pb | 32 % | 32 % | |
| Tin, Sn | 16 % | 16 % |
Users viewing this material also viewed the following:
- Rogers Corporation Poron® 4701-50-15 Cellular Urethane Foam
- S&E Specialty Polymers GA-2285FR PVC
- SABIC Innovative Plastics Cycoloy® MC5220 PC+ABS (Asia Pacific)
- Ravago Manufacturing Americas Hylex® P1317L Polycarbonate, UV Stabilized, Higher Flow, Mold Release
- LyondellBasell Lupolen® 3020 H LDPE, Film Grade
- Lubriplate H0-3 Petroleum-Based Heavy-Duty Hydraulic Oil
- Haynes 556® alloy, cold rolled, solution annealed sheet, 0.8-2.8 mm thick
- Arlon 51981XA015 0.0150" Uncured Silicone Rubber with Fiberglass Substrate
- 3M FV392 Removable White Vinyl Label Products
Copyright © lookpolymers.com All Rights Reserved