IRPC Polimaxx Porene KU650 Acrylonitrile Butadiene Styrene
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | IRPC Polimaxx |
| Trade Name | Porene |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | IRPC Polimaxx Porene KU650 Acrylonitrile Butadiene Styrene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications:injection moldingautomotive parts such as instrument panels, console boxes, switches, automotive louvers, ectelectrical appliances
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 1.8 g/10 min @Load 10.0 kg, Temperature 220 °C |
1.8 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 110 @Thickness 6.35 mm, Temperature 23.0 °C |
110 @Thickness 0.250 in, Temperature 73.4 °F |
ASTM D785 |
| Tensile Strength, Ultimate | 44.1 MPa @Temperature 23.0 °C |
6400 psi @Temperature 73.4 °F |
ASTM D638 |
| Flexural Yield Strength | 63.7 MPa @Temperature 23.0 °C |
9250 psi @Temperature 73.4 °F |
ASTM D790 |
| Flexural Modulus | 2.06 GPa @Temperature 23.0 °C |
299 ksi @Temperature 73.4 °F |
ASTM D790 |
| Izod Impact, Notched | 1.37 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
2.57 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C @Thickness 6.35 mm |
252 °F @Thickness 0.250 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 113 °C @Thickness 6.35 mm |
235 °F @Thickness 0.250 in |
ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
|
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 200 - 270 °C | 392 - 518 °F | |
| Drying Temperature | 85.0 - 95.0 °C @Time 7200 - 18000 sec |
185 - 203 °F @Time 2.00 - 5.00 hour |
Users viewing this material also viewed the following:
- Nye Lubricants 734A-MS (RL) Synthetic Oil
- Ferro EG 2012 Low-Temperature Sealing
- SABIC Innovative Plastics LNP Thermocomp PK0049 PA 6 (Europe-Africa-Middle East)
- Solvay TECHNYL® A 218 PA66, 33% glass fiber, Conditioned
- A. Schulman POLYFORT™ FXP 1943 CaC03 and Glass Fiber Hybrid Copolymer Polypropylene
- BCC Products BC 5200 Kwik-Set Adhesive
- 3M SJ5700 Protective Product, Molded Shapes
- Akro-Plastic Akromid® B3 GF 30 S1 NAT. (1383) PA, Cold-Impact Resistant, 30% Glass Filled, Natural
- Axiall 12840 Coax & Telecom Flexible PVC
- ATI Allegheny Ludlum Stainless Steel Type 439/AL 439HP™, 50% cold work (ASTM XM-8; UNS S43035)
Copyright © lookpolymers.com All Rights Reserved