IRPC Polimaxx Polene 1100NK Polypropylene Homopolymer
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | IRPC Polimaxx |
| Trade Name | Polene |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | IRPC Polimaxx Polene 1100NK Polypropylene Homopolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
CHARACTERISTICS: HIGH FLOWAPPLICATIONS: FOR INJECTION MOLDING GENERAL PURPOSE : HOUSEWARES, CLOSURES, FOOD CONTAINERS
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 11 g/10 min @Load 2.16 kg, Temperature 230 °C |
11 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 110 | 110 | ASTM D785 |
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | ASTM D638 |
| Elongation at Yield | 36 % | 36 % | ASTM D638 |
| Flexural Modulus | 1.50 GPa | 218 ksi | 1% Secant; ASTM D790 |
| Charpy Impact, Notched | 0.290 J/cm² @Temperature 23.0 °C |
1.38 ft-lb/in² @Temperature 73.4 °F |
DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Lanxess Pocan® B 1501 000000 PBT
- Styron CALIBREâ„¢ 7103-8 Polycarbonate
- Teknor Apex Monprene® MP 1643L1 Thermoplastic Elastomer
- SABIC Innovative Plastics LNP THERMOCOMP PF006U PA 6 (Europe-Africa-Middle East)
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, Hardness 90A, Non-Black Peroxide Cure
- Cossa Polimeri ESTABLEND PA 3000 ABS / Nylon 6 Blend
- DuPont Performance Polymers Sorona® 3301 NC010 Polytrimethylene Terephthalate (PTT) (Unverified Data**)&l
- Arlon Red Silicone Press Pad with Fiberglass Substrate (55393R045)
Copyright © lookpolymers.com All Rights Reserved