Huntsman PE1753 EVA Film Extrusion (discontinued **)
| Category | Polymer , Film , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate Copolymer (EVA), Film Grade |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Huntsman PE1753 EVA Film Extrusion
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
7.5% Vinyl Acetate EVA copolymer and FDA compliantFeatures: Yields film with good clarity and excellent impact strength.Applications: Film extrusion: icebags, liquid packaging, lamination film, and medical tubing.FDA Notes: Conforms to FDA regulation 21 CFR 177.1350 under condition of use C through G described in Table 2 of 21 CFR 176.170Film properties based on 1.0 guage (25 µm) thickness; blow-up ratio 2:1.Information provided by Huntsman Corporation
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.928 g/cc | 0.0335 lb/in³ | ASTM D1505 |
| Thickness | 25.4 microns | 1.00 mil | |
| Melt Flow | 1.2 g/10 min | 1.2 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 44 | 44 | ASTM D2240 |
| Tensile Strength, Ultimate | 16.0 MPa | 2320 psi | ASTM D638 |
| Tensile Strength, Yield | 8.00 MPa | 1160 psi | ASTM D638 |
| Film Elongation at Break, MD | 250 % | 250 % | ASTM D882 |
| Film Elongation at Break, TD | 400 % | 400 % | ASTM D882 |
| Elongation at Break | 1000 % | 1000 % | ASTM D638 |
| Modulus of Elasticity | 0.138 GPa | 20.0 ksi | Secant; ASTM D638 |
| Secant Modulus, MD | 0.104 GPa | 15.1 ksi | ASTM D882 |
| Secant Modulus, TD | 0.110 GPa | 16.0 ksi | ASTM D882 |
| Dart Drop | 11.0 g/micron | 280 g/mil | ASTM D1709 |
| Dart Drop Test | 280 g | 0.617 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 24.0 MPa | 3480 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 22.0 MPa | 3190 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 79.0 °C | 174 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 5.0 % | 5.0 % | ASTM D1003 |
| Gloss | 70 % | 70 % | at 45°; ASTM D523 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 193 - 204 °C | 379 - 399 °F |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Rigid Extrusion L0148 Polyvinyl Chloride, Rigid (PVC, Rigid)
- Ovation Polymers Opnyl OP6GF15 Nylon 6, 15% Glass Reinforced, Conditioned
- Kotec Carbotex K-30FRT12 Polycarbonate, Flame Retardant
- Microtherm Group MT Thermosphere® Moldable Insulation Paste
- Lehmann & Voss LUVOCOM® 1-1119 VP Polyamide 66, with carbon fiber, heat stabilized
- Lanxess Durethan® TP 142-011 900116 Nylon 6
- Akro-Plastic Akromid® S3 GF15 1 (3223) PA 6.10 Conditioned, 15% Glass Filled
- Beijing Ranger Chem 194 Solid Epoxy Resin
Copyright © lookpolymers.com All Rights Reserved