Arlon R35551X015 0.015" Uncured Silicone Rubber with Woven Fabric Substrate

Category Polymer , Thermoset , Silicone , Silicone Rubber
Manufacturer Arlon
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arlon R35551X015 0.015" Uncured Silicone Rubber with Woven Fabric Substrate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Design/Construction:Interleave: 0.003" PolyethyleneSide 1: Uncured Silicone RubberSubstrate: Primed 3M Nextel 312 Woven Fabric AF-10, HCSide 2: Uncured Silicone RubberThis data represents typical values for the production material and should not be used as material specifications.Information provided by ARLON Silicone Technologies Division.
Physical Properties Metric English Comments
Density 1.32 g/cc
0.0477 lb/in³
Silicone Property; Arlon SQA-TMS-024
Thickness 76.2 microns
3.00 mil
Side 1; Arlon SQA-TMS-003
76.2 microns
3.00 mil
Side 2; Arlon SQA-TMS-003
229 microns
9.00 mil
Substrate; Arlon SQA-TMS-003
381 microns
15.0 mil
Overall thickness; Arlon SQA-TMS-003
Mechanical Properties Metric English Comments
Hardness, Shore A 42
42
Silicone Property; ASTM D2240
Tensile Strength 5.83 MPa
845 psi
Silicone Property; ASTM D412
Elongation at Break 500 %
500 %
Silicone Property; ASTM D412
Peel Strength 1.58 kN/m
9.00 pli
Bond Strength; Arlon SQA-TMS-011
Thermal Properties Metric English Comments
Maximum Service Temperature, Inert 232 °C
450 °F
Minimum Service Temperature, Air -56.7 °C
-70.0 °F
Processing Properties Metric English Comments
Cure Time 120 min

@Temperature 204 °C
2.00 hour

@Temperature 400 °F
Recommended Post Cure Cycle
15.0 min

@Pressure 0.345 MPa,
Temperature 121 °C
0.250 hour

@Pressure 50.0 psi,
Temperature 250 °F
Recommended Cure Cycle
Shelf Life 6.00 Month

@Temperature 21.1 °C
6.00 Month

@Temperature 70.0 °F
Descriptive Properties Value Comments
Color Gray
Product
White
Substrate
Total Product Weight (oz/yd2) 17.2
Arlon SQA-TMS-025