Huntsman IROGRAN® CA116-203 TPU-Polyester
| Category | Polymer , Thermoplastic , Polyurethane, TP , Thermoplastic Polyurethane (TPUR), Polyester Grade |
| Manufacturer | Huntsman Corporation |
| Trade Name | IROGRAN® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Huntsman IROGRAN® CA116-203 TPU-Polyester.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Introduction: IROGRAN CA116-203 is a high performance polyester based thermoplastic polyurethane intended for flat die extrusion applications. IROGRAN CA116-203 is part of the HUNTSMAN film and sheet product range and offers a specially designed, flexible plasticizer free product suitable for the preparation of extruded films with enhanced adhesion following lamination. Performance Features: Low melt temperature High crystallization rate Good low temperature flexibility Good processability Applications: Adhesive film Lamination Information provided by Alliance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | ASTM D792 |
| Melt Index of Compound | 59 g/10 min @Load 5.00 kg, Temperature 190 °C |
59 g/10 min @Load 11.0 lb, Temperature 374 °F |
MVR, [cm<sup>3</sup>/10 min] |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 95 | 95 | Injection molded parts; ASTM D2240 |
| Tensile Strength at Break | 10.0 MPa | 1450 psi | Injection molded parts; DIN 53504 |
| Elongation at Break | 600 % | 600 % | Injection molded parts; DIN 53504 |
| 100% Modulus | 0.00300 GPa | 0.435 ksi | Injection molded parts; DIN 53504 |
| 300% Modulus | 0.00400 GPa | 0.580 ksi | Injection molded parts; DIN 53504 |
| Tear Strength | 80.6 kN/m | 460 pli | Injection molded parts; ASTM D624 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 80.0 - 110 °C | 176 - 230 °F | TMA Melt Range |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 149 °C | 300 °F | Extrusion |
| Middle Barrel Temperature | 154 °C | 309 °F | Extrusion |
| Adapter Temperature | 154 °C | 309 °F | Extrusion |
| Die Temperature | 154 °C | 309 °F | Extrusion |
Users viewing this material also viewed the following:
- NCMT NanoPAC™ N12 High Performance Polypropylene Nanocomposite
- Polykemi AB POLYfill PPH 150DNH Polypropylene Homopolymer, Flame Retardant, Halogen Free
- SABIC Innovative Plastics LNP LUBRICOMP DL002 PC (Europe-Africa-Middle East)
- Albis Plastics Cellulose Acetate Butyrate B9024 (UVI, Odor Mask Added), 10% Plasticizer (discontinued **)
- LG Chemical TR-558NS Transparent ABS, Antistatic, Natural and Colored Pellets
- SABIC Innovative Plastics LNP LUBRICOMP RX05487 PA 66
- Tra-Con Tra-Bond FS25
- Lubrizol ESTANE® 58863 Ether Based Thermoplastic Polyurethane
- ExxonMobil Teresstic 100
- Buckeye Polymers BP FLEX A6310 NAT Thermoplastic Elastomer SEBS
Copyright © lookpolymers.com All Rights Reserved