Huntsman IROGRAN® A 92 E 4860 TPU-Polyester
| Category | Polymer , Thermoplastic , Polyurethane, TP , Thermoplastic Polyurethane (TPUR), Polyester Grade |
| Manufacturer | Huntsman Corporation |
| Trade Name | IROGRAN® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Huntsman IROGRAN® A 92 E 4860 TPU-Polyester.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Introduction: IROGRAN A92E 4860 is a high performance polyester based thermoplastic polyurethane intended for extrusion and injection molding applications. IROGRAN A92E 4860 is part of the HUNTSMAN technical extrusion product range and offers a specially designed, flexible material with a broad processing window particularly suitable for the preparation of spiral tubing, pneumatic tubing, belting and technical moldings.Performance Features: High tensile strength Excellent wear performance Excellent hydrolysis resistance Good low temperature flexibility Information provided by Alliance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | Injection molded parts; ASTM D792 |
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | Injection molded; ASTM D955 |
| Melt Index of Compound | 33 g/10 min @Load 10.0 kg, Temperature 210 °C |
33 g/10 min @Load 22.0 lb, Temperature 410 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 91 | 91 | Injection molded parts; ASTM D2240 |
| Hardness, Shore D | 42 | 42 | Injection molded parts; ASTM D2240 |
| Tensile Strength at Break | 49.0 MPa | 7110 psi | Injection molded parts; DIN 53504 |
| Elongation at Break | 590 % | 590 % | Injection molded parts; DIN 53504 |
| 100% Modulus | 0.00750 GPa | 1.09 ksi | Injection molded parts; DIN 53504 |
| 300% Modulus | 0.0160 GPa | 2.32 ksi | Injection molded parts; DIN 53504 |
| Tear Strength | 116 kN/m | 660 pli | Injection molded parts; ASTM D624 |
| Abrasion | 25 | 25 | mm<sup>3</sup>, Injection molded; DIN 53516 |
| Compression Set | 25 % @Temperature 22.8 °C, Time 252000 sec |
25 % @Temperature 73.0 °F, Time 70.0 hour |
Injection molded; ASTM D395 |
| 39 % @Temperature 70.0 °C, Time 86400 sec |
39 % @Temperature 158 °F, Time 24.0 hour |
Injection molded; ASTM D395 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 188 °C | 370 °F | peak; 0.025" extruded film |
| 180 - 200 °C | 356 - 392 °F | 0.025" extruded film, |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 25.0 - 40.0 °C | 77.0 - 104 °F | Extrusion |
| Middle Barrel Temperature | 200 - 210 °C | 392 - 410 °F | Extrusion |
| Nozzle Temperature | 200 - 210 °C | 392 - 410 °F | Extrusion |
| 210 - 225 °C | 410 - 437 °F | Injection | |
| Adapter Temperature | 200 - 210 °C | 392 - 410 °F | Extrusion |
| Die Temperature | 200 - 210 °C | 392 - 410 °F | Extrusion |
| Melt Temperature | 205 - 220 °C | 401 - 428 °F | Injection |
| Mold Temperature | 20.0 - 70.0 °C | 68.0 - 158 °F | Injection |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Heating Zone | 190-220°C | Injection |
Users viewing this material also viewed the following:
- Overview of materials for Polycarbonate/PET Polyester Blend
- GRECO ISOTHANE 3095A Polyether TPU Resin
- Latrobe LSSâ„¢ Chipper Knife Tool Steel (ASTM A8 Mod.)
- Solvay TECHNYL® B 218L V30 Black 44 N PA66, 30% glass fiber, Conditioned
- Universal Wire Works 617 Nickel Alloy Welding Wire
- A. Schulman POLYFLAM™ CFP 4611 11% CACO3 filled copolymer polypropylene product
- DuPont Performance Polymers Zytel® FG42A NC010 Nylon 66 (Unverified Data**)
- Dow Tyril® 100 SAN
- Ascend Performance Materials Vydyne® 25WSP Nylon 66, Conditioned (2.5% Moisture)
- Kennametal Stellite Stellite® 25 Cobalt Chromium Cast Alloy
Copyright © lookpolymers.com All Rights Reserved