Huntsman IROGRAN® A 80 H 4698 Polyester-Based TPU-Injection Molding Grade
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyurethane TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Polyester Grade |
| Manufacturer | Huntsman Corporation |
| Trade Name | IROGRAN® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Huntsman IROGRAN® A 80 H 4698 Polyester-Based TPU-Injection Molding Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Introduction: IROGRAN A 80 H 4698 is a transparent thermoplastic polyester-polyurethane for injection molding applications. Additional characteristics of the product are good melt flow and easy demolding also for undercut. Performance Features: Easy demolding Good melt flow High transparency High elasticity Low-temperature flexibilityApplications: For the production of casual shoe soles, o-rings screens, technical parts.
Information provided by Huntsman
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | ASTM D995 |
| Melt Index of Compound | 50 g/10 min @Load 21.6 kg, Temperature 190 °C |
50 g/10 min @Load 47.6 lb, Temperature 374 °F |
cm<sup>3</sup>/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 81 | 81 | ASTM D2240 |
| Hardness, Shore D | 31 | 31 | ASTM D2240 |
| Tensile Strength at Break | 47.0 MPa | 6820 psi | DIN 53504 |
| Elongation at Break | 650 % | 650 % | DIN 53504 |
| 100% Modulus | 0.00590 GPa | 0.856 ksi | DIN 53504 |
| 300% Modulus | 0.0150 GPa | 2.18 ksi | DIN 53504 |
| Rebound | 42 % | 42 % | Bayshore; ASTM D2632 |
| Tear Strength | 103 kN/m | 590 pli | ASTM D624 |
| Abrasion | 30 | 30 | [mm<sup>3</sup>]; ISO 4649 |
| Compression Set | 25 % @Temperature 23.0 °C, Time 252000 sec |
25 % @Temperature 73.4 °F, Time 70.0 hour |
ASTM D395 |
| 40 % @Temperature 70.0 °C, Time 86400 sec |
40 % @Temperature 158 °F, Time 24.0 hour |
ASTM D395 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 125 - 180 °C | 257 - 356 °F | Huntsman/TMA |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 90 % | 90 % | transparent; thickness not reported |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 25.0 - 40.0 °C | 77.0 - 104 °F | Extrusion |
| Front Barrel Temperature | 165 - 190 °C | 329 - 374 °F | Extrusion |
| Nozzle Temperature | 170 - 200 °C | 338 - 392 °F | Extrusion |
| 179 - 299 °C | 354 - 570 °F | Injection | |
| Adapter Temperature | 175 - 195 °C | 347 - 383 °F | Extrusion |
| Die Temperature | 175 - 200 °C | 347 - 392 °F | Extrusion |
| Melt Temperature | 170 - 195 °C | 338 - 383 °F | Injection |
| Mold Temperature | 20.0 - 70.0 °C | 68.0 - 158 °F | Injection |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Heating Zone | 175-195°C | Injection |
Users viewing this material also viewed the following:
- Plaskolite West Optix® CA-82 UVA UV-Absorbing Acrylic Resin
- LyondellBasell Plexar® PX5335 Extrudable Tie-Layer Resin, Anhydride Modified LLDPE
- LG Chemical LS100E PVC
- Latrobe Lescalloy® 4340 VAC-ARC ; 10.5" square High Strength Alloy Steel
- SABIC Innovative Plastics LNP VERTON RVL28 PA 66
- Teknor Apex Uniprene® UN-2678C Thermoplastic Vulcanizate
- Dow LDPE 609A Low Density Polyethylene, High Clarity Film Grade
- 3M 1532 Sandblast Stencil
- Guarniflon PTFE G412 Polytetrafluoroethylene 15% Graphite
Copyright © lookpolymers.com All Rights Reserved